Influences of Ag addition to Sn-58Bi solder on SnBi/Cu interfacial reaction

被引：68
|
作者：
Hu, F. Q. [1 ]
Zhang, Q. K. [1 ]
Jiang, J. J. [1 ]
Song, Z. L. [1 ]
机构：
[1] Chinese Acad Sci, Ningbo Inst Mat Technol & Engn, Ningbo 315201, Zhejiang, Peoples R China
来源：
MATERIALS LETTERS | 2018年 / 214卷
关键词：
SnBi solder; Bi segregation; Ag addition; Interfacial embrittlement; Deformation and fracture; Interface; MECHANICAL-PROPERTIES; ALLOYING SUBSTRATE; TENSILE PROPERTIES; BI SEGREGATION; JOINTS; EMBRITTLEMENT; TEMPERATURE; MELT;
D O I：
10.1016/j.matlet.2017.11.127
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In this study, the influences of Ag addition to Sn-58Bi solder on SnBi/Cu interfacial reaction and fracture behavior of the aged SnBiAg/Cu solder joints were investigated. The results reveal that the Ag element in the solder can diffuse into the Cu substrate during the soldering and aging process, forming a Cu-Ag alloy layer around the joint interface. The Bi segregation was not observed at the aged SnBiAg/Cu interface, and the embrittlement will not occur at the aged SnBiAg/Cu solder joints once the Bi segregation was restrained. (C) 2017 Elsevier B.V. All rights reserved.
引用
收藏
页码：142 / 145
页数：4
相关论文
共 50 条
  • [31] Microstructure and Property Changes in Cu/Sn-58Bi/Cu Solder Joints during Thermomigration
    Shen, Yu-An
    Zhou, Shiqi
    Li, Jiahui
    Tu, K. N.
    Nishikawa, Hiroshi
    2019 IEEE 69TH ELECTRONIC COMPONENTS AND TECHNOLOGY CONFERENCE (ECTC), 2019, : 2003 - 2008
  • [32] Effect of Interfacial Reaction in Sn-Ag-Cu Solder Alloy with Ni Addition
    Watanabe, Hirohiko
    Shimoda, Masayoshi
    Hidaka, Noboru
    Shohji, Ikuo
    FRACTURE AND STRENGTH OF SOLIDS VII, PTS 1 AND 2, 2011, 462-463 : 247 - +
  • [33] Interfacial reaction and growth behavior of IMCs layer between Sn-58Bi solders and a Cu substrate
    Hu, Xiaowu
    Li, Yulong
    Min, Zhixian
    JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2013, 24 (06) : 2027 - 2034
  • [34] Influence of Phase Inhomogeneity on Electromigration Behavior in Cu/Sn-58Bi/Cu Solder Joint
    Qin, Hongbo
    Luan, Xinghe
    Yue, Wu
    JOURNAL OF ELECTRONIC MATERIALS, 2019, 48 (06) : 3410 - 3414
  • [35] Influence of Phase Inhomogeneity on Electromigration Behavior in Cu/Sn-58Bi/Cu Solder Joint
    Hongbo Qin
    Xinghe Luan
    Wu Yue
    Journal of Electronic Materials, 2019, 48 : 3410 - 3414
  • [36] Reliability of Graphene Nanosheets-Reinforbed Sn-58Bi/Cu Solder Joints
    Jiang Nan
    Zhang Liang
    Xu Kaikai
    Wang Fengjiang
    Long Weimin
    RARE METAL MATERIALS AND ENGINEERING, 2021, 50 (07) : 2293 - 2299
  • [37] Effects of Sn-Ag-x layers on the solderability and mechanical properties of Sn-58Bi solder
    Zhang S.
    Liu Y.
    Zhang H.
    Zhou M.
    Xue Y.
    Zeng X.
    Cao R.
    Chen P.
    Welding International, 2021, 35 (1-3): : 16 - 23
  • [38] Microstructure and mechanical properties of Ag nanoparticles-modified Sn-58Bi/Cu solder joints during liquid-state reaction
    Park, Dae-Young
    Kim, Jungsoo
    Yu, Dong-Yurl
    Yoo, Sehoon
    Park, Hyun-Soon
    Sohn, Yoonchul
    Ko, Yong-Ho
    JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2021, 32 (24) : 28346 - 28357
  • [39] Effects of Minor Addition of Cu and Ni on the Microstructure, Thermal and Mechanical Properties, and Wettability of Sn-58Bi Solder Alloys
    Sungkhaphaitoon, Phairote
    Chantaramanee, Suchart
    JOURNAL OF ELECTRONIC MATERIALS, 2025, : 4154 - 4165
  • [40] Influences of low In alloying and aging on microstructure and plastic deformation behavior of Sn-58Bi solder
    Zhang, He
    Zhang, Qingke
    Song, Zhenlun
    JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2024, 35 (17)
12345