Failure analysis of stainless steel bellows

被引：0
|
作者：
Shaikh, H [1 ]
George, G [1 ]
Khatak, HS [1 ]
机构：
[1] Indira Gandhi Ctr Atom Res, Corros Sci & Technol Div, Kalpakkam 603102, Tamil Nadu, India
来源：
PRAKTISCHE METALLOGRAPHIE-PRACTICAL METALLOGRAPHY | 2001年 / 38卷 / 09期
关键词：
Steel corrosion - Residual stresses - Bellows - Stainless steel - Sodium hydroxide - Stress corrosion cracking;
D O I：
10.1515/pm-2001-380906
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Two bellow sealed valves used to control the flow of sodium in pipelines of the Component Testing Facility (CTF) at the Indira Gandhi Centre for Atomic Research (IGCAR), Kalpakkam, failed prematurely. The failure of both these valves occurred by intergranular stress corrosion cracking (IGSCC) of the stainless steel bellows. This premature failure occurred in the sensitised stainless steel of the bellows due to the conjoint action of high tensile stresses, caused by superimposition of operating stresses over residual stresses, and sodium hydroxide environment which was formed by reaction between sodium and moisture in the cover gas.
引用
收藏
页码：532 / 537
页数：6
相关论文
共 50 条
  • [31] Failure analysis of service exposed austenitic stainless steel pipelines
    Sreevidya, N.
    Abhijith, S.
    Albert, Shaju K.
    Vinod, V.
    Banerjee, Indranil
    ENGINEERING FAILURE ANALYSIS, 2020, 108
  • [32] Failure analysis of a fractured stainless steel femoral bone plate
    Fantin, Luiza de Brito
    Moreira, Marcelo Ferreira
    de Souza, Jose Marcos Paz
    ENGINEERING FAILURE ANALYSIS, 2025, 173
  • [33] Failure analysis of a weld-decayed austenitic stainless steel
    Song, Ming
    Guan, Kaishu
    ENGINEERING FAILURE ANALYSIS, 2011, 18 (06) : 1613 - 1618
  • [34] Corrosion failure analysis of duplex stainless steel in marine environment
    Wang, Haipeng
    Yang, Yang
    Yang, Zhongna
    Xu, Zhigang
    Chai, Yuanyuan
    Zhang, Zhuwu
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2022, 17 (05):
  • [35] Failure analysis of stainless steel metal hose used for welding
    Kim, Youngsik
    Choe, Byunghak
    Han, Sunghee
    Kim, Daehyun
    Kim, Jinha
    Choi, Kwangsoo
    Kim, Hunbae
    Choi, Seokyeol
    ENGINEERING FAILURE ANALYSIS, 2024, 163
  • [36] Failure analysis of a martensitic stainless steel steam turbine blade
    Ruchert, Cassius Olivio Figueiredo Terra
    Carvalho, Marcio
    JOURNAL OF THE BRAZILIAN SOCIETY OF MECHANICAL SCIENCES AND ENGINEERING, 2024, 46 (07)
  • [37] FAILURE ANALYSIS OF STAINLESS-STEEL AT ELEVATED-TEMPERATURES
    SCIAMMARELLA, CA
    RAO, MPK
    EXPERIMENTAL MECHANICS, 1978, 18 (05) : N36 - N36
  • [38] Failure analysis of a brazed, stainless steel fuel injection line
    Kral, Milo V.
    Maher, Cynthia M.
    McSwain, Richard H.
    ENGINEERING FAILURE ANALYSIS, 2018, 88 : 54 - 62
  • [39] Microstructural analysis of failure of a stainless steel bone plate implant
    E. Proverbio
    L. M. Bonaccorsi
    Practical Failure Analysis, 2001, 1 (4) : 33 - 38
  • [40] Analysis of failure due to SCC in stainless steel stove shell
    Pan, Xide
    Shen, Fenggang
    Dong, Junming
    Xue, Jin
    Han Jie/Welding & Joining, (02): : 9 - 12
12345