Influence of Sharpness of Stress Concentrators on Crack Growth Resistance of Molybdenum

被引:0
|
作者
Koval, O. Yu. [1 ]
机构
[1] Natl Acad Sci Ukraine, IN Frantsevich Inst Mat Sci Problems, UA-03142 Kiev, Ukraine
来源
METALLOFIZIKA I NOVEISHIE TEKHNOLOGII | 2011年 / 33卷 / 06期
关键词
D O I
暂无
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Behaviour of fracture toughness of molybdenum alloys is studied in a wide temperature range with consideration of fracture mechanisms on a microlevel. Molybdenum alloy CM-10 is chosen for this study. It manifests the most complete set of fracture mechanisms in the temperature range of brittle-ductile transition. The obtained temperature dependence of fracture toughness is analysed with regard for a sharpness of crack.
引用
收藏
页码:841 / 851
页数:11
相关论文
共 50 条
  • [21] Influence of Molybdenum and Phosphorus on the Stress Corrosion Resistance of Austenitic Stainless Steels.
    Faty, Sana
    Da Cunha Belo, M.
    Metaux corrosion-industries, 1982, 57 (681): : 173 - 179
  • [22] NUMERICAL INVESTIGATION ON THE INFLUENCE OF RESIDUAL STRESSES ON DUCTILE CRACK GROWTH RESISTANCE
    Ren, X. B.
    Zhang, Z. L.
    Nyhus, B.
    PROCEEDINGS OF THE ASME 29TH INTERNATIONAL CONFERENCE ON OCEAN, OFFSHORE AND ARCTIC ENGINEERING 2010, VOL 2, 2010, : 787 - 794
  • [24] Influence of crack closure and local near-tip stress on crack growth life estimation
    Savkin, A. N.
    Sunder, R.
    Denisevich, D. S.
    Badikov, K. A.
    Sedov, A. A.
    2ND INTERNATIONAL CONFERENCE ON STRUCTURAL INTEGRITY AND EXHIBITION 2018 (SICE 2018), 2019, 14 : 429 - 434
  • [25] Flaw Resistance as a Measure of Brittle Failure Resistance of Steels with Stress Concentrators.
    Zlenko, G.P.
    Mettus, G.S.
    Meshkov, Yu.Ya.
    Nikonenko, D.I.
    Frenkel', K.L.
    Problemy Prochnosti, 1986, (05): : 75 - 80
  • [26] THE INFLUENCE OF THE CRACK TIP STRESS-FIELD ON THE NUCLEATION AND GROWTH OF VOIDS
    JAGANNADHAM, K
    MATERIALS SCIENCE AND ENGINEERING, 1983, 60 (02): : 95 - 108
  • [27] A study on the influence of stress concentration in DFZ on the growth of model I crack
    Fu, Hao
    Chen, Jian
    Ren, Yanjie
    He, Jianjun
    Sun, Qingmin
    Hu, Min
    TRANSFERABILITY AND APPLICABILITY OF CURRENT MECHANICS APPROACHES, 2009, : 189 - 193
  • [28] TEST PROCEDURE FOR DETERMINING INFLUENCE OF STRESS RATIO ON FATIGUE CRACK GROWTH
    FITZGERALD, JH
    WEI, RP
    JOURNAL OF TESTING AND EVALUATION, 1974, 2 (02) : 67 - 70
  • [29] INFLUENCE OF R ON EFFECTIVE STRESS RANGE RATIO AND CRACK-GROWTH
    SRIVASTAVA, YP
    GARG, SBL
    ENGINEERING FRACTURE MECHANICS, 1985, 22 (06) : 915 - 926
  • [30] INFLUENCE OF STRESS STATE ON STATIC CRACK GROWTH IN ALZNMGCUO.5
    SCHWALBE, KH
    ENGINEERING FRACTURE MECHANICS, 1977, 9 (03) : 557 - 583