The determination of the influence of pH value of curing conditions on Portland cement hydration

被引：27
|
作者：
Siler, Pavel [1 ]
Kolarova, Iva [1 ]
Sehnal, Tomas [1 ]
Masilko, Jiri [1 ]
Opravil, Tomas [1 ]
机构：
[1] Brno Univ Technol, Fac Chem, Ctr Mat Res, CS-61090 Brno, Czech Republic
来源：
ECOLOGY AND NEW BUILDING MATERIALS AND PRODUCTS 2016 | 2016年 / 151卷
关键词：
Portland cement; mechanical properties; thermal analysis; X-ray diffraction; pH value; COMPRESSIVE STRENGTH; REGIMES; MORTARS;
D O I：
10.1016/j.proeng.2016.07.393
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
Water composition during cement hydration can be changed due to migration of ions from the cement matrix to the solution. The storage of various materials together can lead to transfer of various ions and distortion of results. This article is aimed on the influence of storage environment on the Portland cement hydration and hydrated samples composition. Test specimens were prepared and stored in different environments. Storage environments were ultrapure water and solutions having alkaline and acidic pH value. The mechanical properties were measured after 1, 7 and 28 days. Composition of samples stored in different environment was tested by X-ray diffraction and DTA analysis. (C) 2016 Published by Elsevier Ltd. This is an open access article under the CC BY-NC-ND license.
引用
收藏
页码：10 / 17
页数：8
相关论文
共 50 条
  • [21] Influence of superplasticizers on the course of Portland cement hydration
    Pavel Šiler
    Iva Kolářová
    Josef Krátký
    Jaromír Havlica
    Jiří Brandštetr
    Chemical Papers, 2014, 68 : 90 - 97
  • [22] Influence of superplasticizers on the course of Portland cement hydration
    Siler, Pavel
    Kolarova, Iva
    Kratky, Josef
    Havlica, Jaromir
    Brandstetr, Jiri
    CHEMICAL PAPERS, 2014, 68 (01) : 90 - 97
  • [23] Influence of Sucrose on Hydration Process of Portland Cement
    Li Zhenghao
    Shen Weiguo
    Lan Qing
    Lu Zili
    Cao Lianghong
    Xu Zhiyuan
    SILICATE BUILDING MATERIALS - SBM 2013, 2014, 599 : 46 - +
  • [24] Influence of ultradispersed silicas on Portland cement hydration
    Brykov, A. S.
    Kamaliev, R. T.
    Mokeev, M. V.
    RUSSIAN JOURNAL OF APPLIED CHEMISTRY, 2010, 83 (02) : 208 - 213
  • [25] INFLUENCE OF CURING AT DIFFERENT RELATIVE HUMIDITIES ON THE HYDRATION AND POROSITY OF A PORTLAND FLY-ASH CEMENT PASTE
    KILLOH, DC
    PARROTT, LJ
    PATEL, RG
    FLY ASH, SILICA FUME, SLAG, AND NATURAL POZZOLANS IN CONCRETE, VOL 1-2, 1989, 114 : 157 - 174
  • [26] HYDRATION OF PORTLAND CEMENT
    CHATTERJ.AK
    PHATAK, TC
    RAWAT, RS
    NATURE, 1965, 207 (4998) : 711 - &
  • [27] The influence of ethanolamines on the hydration and mechanical properties of Portland cement
    Heren, Z
    Olmez, H
    CEMENT AND CONCRETE RESEARCH, 1996, 26 (05) : 701 - 705
  • [28] Influence of Organic Esters on Portland Cement Hydration and Hardening
    Li, Duan-le
    Zheng, Da-peng
    Wang, Dong-min
    Zhao, Ji-hui
    Du, Cheng
    Ren, Cai-fu
    ADVANCES IN MATERIALS SCIENCE AND ENGINEERING, 2018, 2018
  • [29] Influence of Cellulose Ethers on Hydration Products of Portland Cement
    马保国
    欧志华
    Journal of Wuhan University of Technology(Materials Science), 2011, (03) : 588 - 593
  • [30] Influence of active alumina on the hydration process of Portland cement
    Novotny, Radoslav
    Bartonickova, Eva
    Svec, Jiri
    Moncekova, Miroslava
    ECOLOGY AND NEW BUILDING MATERIALS AND PRODUCTS 2016, 2016, 151 : 80 - 86
12345