The determination of the influence of pH value of curing conditions on Portland cement hydration

被引：27
|
作者：
Siler, Pavel [1 ]
Kolarova, Iva [1 ]
Sehnal, Tomas [1 ]
Masilko, Jiri [1 ]
Opravil, Tomas [1 ]
机构：
[1] Brno Univ Technol, Fac Chem, Ctr Mat Res, CS-61090 Brno, Czech Republic
来源：
ECOLOGY AND NEW BUILDING MATERIALS AND PRODUCTS 2016 | 2016年 / 151卷
关键词：
Portland cement; mechanical properties; thermal analysis; X-ray diffraction; pH value; COMPRESSIVE STRENGTH; REGIMES; MORTARS;
D O I：
10.1016/j.proeng.2016.07.393
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
Water composition during cement hydration can be changed due to migration of ions from the cement matrix to the solution. The storage of various materials together can lead to transfer of various ions and distortion of results. This article is aimed on the influence of storage environment on the Portland cement hydration and hydrated samples composition. Test specimens were prepared and stored in different environments. Storage environments were ultrapure water and solutions having alkaline and acidic pH value. The mechanical properties were measured after 1, 7 and 28 days. Composition of samples stored in different environment was tested by X-ray diffraction and DTA analysis. (C) 2016 Published by Elsevier Ltd. This is an open access article under the CC BY-NC-ND license.
引用
收藏
页码：10 / 17
页数：8
相关论文
共 50 条
  • [1] Influence of curing temperature on belite cement hydration: A comparative study with Portland cement
    Shirani, Shiva
    Cuesta, Ana
    Morales-Cantero, Alejandro
    De la Torre, Angeles G.
    Olbinado, Margie P.
    Aranda, Miguel A. G.
    CEMENT AND CONCRETE RESEARCH, 2021, 147
  • [2] Influence of curing temperature on hydration and microstructural development of ordinary Portland cement
    Emmanuel, Arun C.
    Krishnan, Sreejith
    Bishnoi, Shashank
    CONSTRUCTION AND BUILDING MATERIALS, 2022, 329
  • [3] DEGREE OF HYDRATION OF PORTLAND CEMENT PASTES WITH LOW WATER/CEMENT RATIOS AS INFLUENCED BY CURING CONDITIONS
    HANNA, KM
    ELHEMALY, SA
    JOURNAL OF APPLIED CHEMISTRY, 1970, 20 (04): : 117 - +
  • [4] Influence of curing temperatures on the hydration of calcium aluminate cement/Portland cement/calcium sulfate blends
    Xu, Linglin
    Wu, Kai
    Roessler, Christiane
    Wang, Peiming
    Ludwig, H. M.
    CEMENT & CONCRETE COMPOSITES, 2017, 80 : 298 - 306
  • [5] Influence of curing temperature on the hydration and strength development of Class G Portland cement
    Pang, Xueyu
    Sun, Lijun
    Chen, Min
    Xian, Ming
    Cheng, Guodong
    Liu, Yang
    Qin, Jiankun
    CEMENT AND CONCRETE RESEARCH, 2022, 156
  • [6] Insights into the hydration of Portland cement under hydrothermal curing
    Martin T. Palou
    Eva Kuzielová
    Matúš Žemlička
    Jakub Tkácz
    Jiří Másilko
    Journal of Thermal Analysis and Calorimetry, 2019, 138 : 4155 - 4165
  • [7] The effect of curing temperature on the hydration of binary Portland cement
    Palou, Martin T.
    Kuzielova, Eva
    Zemlicka, Matus
    Bohac, Martin
    Novotny, Radoslav
    JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY, 2016, 125 (03) : 1301 - 1310
  • [8] Insights into the hydration of Portland cement under hydrothermal curing
    Palou, Martin T.
    Kuzielova, Eva
    Zemlicka, Matus
    Tkacz, Jakub
    Masilko, Jiri
    JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY, 2019, 138 (06) : 4155 - 4165
  • [9] Influence of curing conditions on hydration of magnesium silicate hydrate cement
    Li, Xiangguo
    Fu, Qiuyan
    Lv, Yang
    Leng, Difei
    Jiang, Dongbing
    He, Chenhao
    Wu, Kai
    Dan, Jianming
    CONSTRUCTION AND BUILDING MATERIALS, 2022, 361
  • [10] Influence of fly ash and GGBFS on the pH value of cement mortar in different curing conditions
    Shafigh, Payam
    Yousuf, Sumra
    Ibrahim, Zainah
    Alsubari, Belal
    Asadi, Iman
    ADVANCES IN CONCRETE CONSTRUCTION, 2021, 11 (05) : 419 - 428
12345