Centimeter-sized zeolite bodies of intergrown crystals: Preparation, characterization and study of binder evolution

The control of the inter-particle porosity in polycrystalline zeolite bodies remains a challenge. The present study reports on the preparation of centimeter-sized zeolite bodies (32 x 2 mm pellets) with reduced inter-particle porosity. The bodies were prepared by assembling zeolite colloidal nanocrystals with monomodal particle size distribution and sub-colloidal aluminum hydroxide binder. A secondary growth treatment under hydrothermal conditions was performed in order to fill up the inter-particle voids and obtain polycrystalline zeolite materials with textural characteristics close to those of single zeolite crystals. Initial material, intermediates and ultimate product were studied with a combination of complementary methods revealing a substantial reduction even an elimination of the inter-particle porosity. Particular attention was paid to the chemical evolution of the binder and the migration of aluminum species, employing X-ray powder diffraction, Al-27-MAS, Al-27-3QMAS NMR and X-ray fluorescence spectroscopy analyses. Evidences for insertion of aluminum from the binder into the zeolite framework during secondary growth step were found. Consequently the ultimate pellets comprised aluminum-rich zeolite beta crystals and very low binder content. (C) 2010 Elsevier Inc. All rights reserved.