Stress relaxation behavior of lead-free solder joint

被引：0
|
作者：
Zhu, Yongxin [1 ]
Li, Xiaoyan [1 ]
Gao, Ruiting [1 ]
机构：
[1] Beijing Univ Technol, Sch Mat Sci & Engn, Beijing 100024, Peoples R China
来源：
JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS | 2015年 / 26卷 / 05期
基金：
中国国家自然科学基金;
关键词：
STRAIN-RATE; SN-AG; PLASTIC-DEFORMATION; FATIGUE DAMAGE; CREEP; TEMPERATURE; EVOLUTION;
D O I：
10.1007/s10854-015-2792-y
中图分类号：
TM [电工技术]; TN [电子技术、通信技术];
学科分类号：
0808 ; 0809 ;
摘要：
In this work, stress relaxation behavior of Sn3.5Ag0.5Cu solder joint was investigated under 398 K. Three strain ranges (4, 6, and 8 %) and two strain rates (0.002 and 0.01/s) were utilized. The results show that the effect of strain range on stress relaxation is not significant under high strain rate. However, it firstly increases with strain range and then decreases after approaching the maximum value under low strain rate. Moreover, Stress relaxes more under high strain rate than that under low strain rate. Feltham equation can describe the stress relaxation behavior well under high strain rate. After a certain relaxation time, crack appears at the corner of the solder joint and the stress appears to increase a little.
引用
收藏
页码：3020 / 3024
页数：5
相关论文
共 50 条
  • [1] Stress relaxation behavior of lead-free solder joint
    Yongxin Zhu
    Xiaoyan Li
    Ruiting Gao
    Journal of Materials Science: Materials in Electronics, 2015, 26 : 3020 - 3024
  • [2] Lead-free Flux Effect in Lead-free Solder Joint Improvement
    Leng, Eu Poh
    Ding, Min
    Ahmad, Ibrahim
    Jiun, Hoh Huey
    Hazlinda, Kamarudin
    IEMT 2006: 31ST INTERNATIONAL CONFERENCE ON ELECTRONICS MANUFACTURING AND TECHNOLOGY, 2006, : 541 - 548
  • [3] Constraining Effects of Lead-Free Solder Joints During Stress Relaxation
    Zimprich, Peter
    Saeed, Usman
    Weiss, Brigitte
    Ipser, Herbert
    JOURNAL OF ELECTRONIC MATERIALS, 2009, 38 (03) : 392 - 399
  • [4] Constraining Effects of Lead-Free Solder Joints During Stress Relaxation
    Peter Zimprich
    Usman Saeed
    Brigitte Weiss
    Herbert Ipser
    Journal of Electronic Materials, 2009, 38
  • [5] CHARACTERIZATION OF CREEP BEHAVIOR OF ACTUAL LEAD-FREE SOLDER JOINT FOR MODELING
    Lee, Hohyung
    Liu, Ruiyang
    Park, Seungbae
    Kwak, Jae
    PROCEEDINGS OF THE ASME INTERNATIONAL MECHANICAL ENGINEERING CONGRESS AND EXPOSITION, 2014, VOL 10, 2015,
  • [6] Influence of Joint Arrangement on the Fracture Behavior of Lead-Free Solder Joints
    Mirmehdi, Sadegh
    Nourani, Amir
    Honarmand, Mohammadmahdi
    Assempour, Ahmad
    JOURNAL OF ELECTRONIC MATERIALS, 2021, 50 (04) : 2117 - 2128
  • [7] Influence of Joint Arrangement on the Fracture Behavior of Lead-Free Solder Joints
    Sadegh Mirmehdi
    Amir Nourani
    Mohammadmahdi Honarmand
    Ahmad Assempour
    Journal of Electronic Materials, 2021, 50 : 2117 - 2128
  • [8] Effect on lead-free solder joint reliability caused by solder volume
    Yamabe M.
    Fukumitsu M.
    Fukuchi Y.
    Yosetsu Gakkai Shi/Journal of the Japan Welding Society, 2010, 79 (03): : 16 - 21
  • [9] Delantination by reheating in SMD solder joint using lead-free solder
    Momokawa, Y
    Ishizuka, N
    NEC RESEARCH & DEVELOPMENT, 2003, 44 (03): : 251 - 255
  • [10] Impact of solder pad shape on lead-free solder joint reliability
    Vasko, Cyril
    Novotny, Marek
    Szendiuch, Ivan
    2008 31ST INTERNATIONAL SPRING SEMINAR ON ELECTRONICS TECHNOLOGY: RELIABILITY AND LIFE-TIME PREDICTION, 2008, : 443 - 445
12345