Multistage fatigue modeling of single-edge-notch tension specimens for Ni-based superalloy GH4169

被引：4
|
作者：
Wu, Z. R. [1 ]
Liu, F. L. [1 ]
Li, X. [1 ]
Fang, L. [1 ]
Song, Y. D. [1 ]
机构：
[1] Nanjing Univ Aeronaut & Astronaut, State Key Lab Mech & Control Mech Struct, Nanjing 210016, Jiangsu, Peoples R China
来源：
ADVANCES IN MECHANICAL ENGINEERING | 2017年 / 9卷 / 11期
关键词：
Multistage fatigue; small fatigue crack; long fatigue crack; life prediction; GH4169; CRACK-GROWTH; ALUMINUM-ALLOY; MECHANICS ANALYSIS; INITIATION; LIFE;
D O I：
10.1177/1687814017729948
中图分类号：
O414.1 [热力学];
学科分类号：
摘要：
Multistage fatigue tests were conducted on the single-edge-notch tension specimens of Ni-based superalloy GH4169. Fatigue crack growth data at different stages were recorded with the surface replica technique. Continuum damage mechanics incorporating critical distance theory was used to evaluate fatigue crack initiation life. Then, small and long fatigue crack grow rates were modeled using Shyam's model and modified Paris law, respectively. Finally, the multistage fatigue model deriving from the above theories was proposed to predict total fatigue life of GH4169. Fatigue life prediction results show that the proposed multistage fatigue model has high accuracy for GH4169.
引用
收藏
页数：11
相关论文
共 50 条
  • [41] A finite element analysis of thermal relaxation of residual stress in laser shock processing Ni-based alloy GH4169
    Ren, X. D.
    Zhan, Q. B.
    Yuan, S. Q.
    Zhou, J. Z.
    Wang, Y.
    Ren, N. F.
    Sun, G. F.
    Zheng, L. M.
    Dai, F. Z.
    Yang, H. M.
    Dai, W. J.
    MATERIALS & DESIGN, 2014, 54 : 708 - 711
  • [42] The stress intensity factor calculation for combined sliding wear and fatigue of GH4169 superalloy based on three-dimensional simulation
    Wang, Jingchen
    Gao, Yukui
    WEAR, 2019, 436
  • [43] Thermo-mechanical fatigue failure of a single crystal Ni-based superalloy
    Okazaki, M.
    Sakaguchi, M.
    INTERNATIONAL JOURNAL OF FATIGUE, 2008, 30 (02) : 318 - 323
  • [44] Low-cycle Fatigue Behavior of a Cast Ni-based Superalloy K4169 at 650°C
    Liu, Qing'ao
    Zhang, Weihong
    Wang, Zhiyuan
    Sun, Wenru
    Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research, 2024, 38 (08): : 621 - 631
  • [45] Fretting fatigue life improvement of nickel-based superalloy GH4169 dovetail slots by deflecting abrasive waterjet peening process
    Yao, Shu-Lei
    Zeng, Xi -Ting
    Li, Kai-Shang
    Wang, Ji
    Wang, Run-Zi
    Wang, Ning
    Zhang, Cheng-Cheng
    Zhang, Xian-Cheng
    Tu, Shan-Tung
    INTERNATIONAL JOURNAL OF FATIGUE, 2023, 175
  • [46] Numerical Simulation on Residual Stress Field of Flat-Topped Laser Oblique Shocking of Ni-Based Alloy GH4169
    Qu, Xiangming
    Zhang, Yongkang
    Liu, Jun
    ADVANCES IN MATERIALS SCIENCE AND ENGINEERING, 2020, 2020
  • [47] Thermomechanical Fatigue Crack Growth Modeling in a Ni-Based Superalloy Subjected to Sustained Load
    Storgards, Erik
    Simonsson, Kjell
    Sjostrom, Soren
    Moverare, Johan
    JOURNAL OF ENGINEERING FOR GAS TURBINES AND POWER-TRANSACTIONS OF THE ASME, 2016, 138 (01):
  • [48] Thermomechanical fatigue damage mechanism and life assessment of a single crystal Ni-based superalloy
    Yang, Junjie
    Jing, Fulei
    Yang, Zhengmao
    Jiang, Kanghe
    Hu, Dianyin
    Zhang, Bin
    JOURNAL OF ALLOYS AND COMPOUNDS, 2021, 872
  • [49] Low-cycle fatigue behaviour of a Ni-based single-crystal superalloy
    Segersall, Mikael
    Moverare, Johan J.
    Leidermark, Daniel
    Simonsson, Kjell
    11TH INTERNATIONAL FATIGUE CONGRESS, PTS 1 AND 2, 2014, 891-892 : 416 - 421
  • [50] Creep-fatigue life prediction in nickel-based superalloy GH4169 based on microstructural damage quantification with the help of electron backscatter diffraction
    Wang, Run-Zi
    Chen, Hao
    Zhang, Yang
    Zhang, Xian-Cheng
    Tu, Shan-Tung
    MATERIALS & DESIGN, 2020, 195
12345