High electromagnetic interference shielding of poly(ether-sulfone)/multi-walled carbon nanotube nanocomposites fabricated by an eco-friendly route

High-performance polymer matrix nanocomposites based on poly(ether-sulfone) (PES) matrix reinforced with multi-walled carbon nanotubes (MWCNTs) were fabricated using planetary ball mill followed by hot pressing. Their electrical properties and the electromagnetic interference shielding effectiveness (EMI-SE) were investigated and discussed. A percolation threshold of about 0.65 vol% MWCNT was obtained. The electrical conductivity was increased by more than ten orders of magnitude at the percolation threshold and to approximately 0.01 S cm(-1)at 6.67 vol% (or 10 wt%) MWCNT. This is a significant improvement. The highest EMI-SE of about 29-30 dB (both in the X-band and K-u-band) was obtained for the 6.67 vol% MWCNT filled nanocomposites with a thickness of 0.9 mm. The specific EMI-SE of these nanocomposites were found to be higher than the literature values. The thermal stability and the char yield (measured at 900 degrees C) of the nanocomposites were found to be more than 470 degrees C and 40.6%, respectively.