Effect of a magnetic field applied during fusion welding on the fatigue damage of 2205 duplex stainless steel joints

被引：16

作者：

Rosado-Carrasco, J. ^{[1
]}

Krupp, U. ^{[2
]}

Lopez-Morelos, V. H. ^{[3
]}

Giertler, A. ^{[2
]}

Garcia-Renteria, M. A. ^{[4
]}

Gonzalez-Sanchez, J. ^{[1
]}

机构：

[1] Autonomous Univ Campeche, Ctr Corros Res, Av Heroe Nacozari 480,PC 24070, San Francisco Campeche, Cam, Mexico

[2] Univ Appl Sci, Fac Engn & Comp Sci, Osnabruck, Germany

[3] Univ Michoacana, Met & Mat Res Inst, AP 888, Morelia 58000, Michoacan, Mexico

[4] Autonomous Univ Coahuila, Fac Met, Carretera 57 Km 5, Monclova 25720, Coahuila, Mexico

来源：

INTERNATIONAL JOURNAL OF FATIGUE | 2019年 / 121卷

关键词：

Low intensity electromagnetic field; Duplex stainless steel; Gas metal arc welding; Fatigue damage; Microstructure evolution; HIGH-CYCLE-FATIGUE; HEAT-TREATMENT; ELECTROMAGNETIC-INTERACTION; MICROSTRUCTURE EVOLUTION; CORROSION-RESISTANCE; LOCALIZED CORROSION; PITTING CORROSION; SLIP SYSTEMS; BEHAVIOR; IDENTIFICATION;

D O I：

10.1016/j.ijfatigue.2018.12.022

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

The effect of the application of a 3 mT electromagnetic field (EMF) during the welding of a 2205 duplex stainless steel on the resistance to fatigue damage was investigated on samples subjected to high cycle fatigue (HCF) and very high cycle fatigue (VHCF) conditions. Ferrite grain refinement, high volume fraction of regenerated austenite in the heat affected zone and smaller columnar grains in the weld metal were induced by (EMF) application during gas metal arc welding. The improved microstructure evolution during the thermal cycle increased the number of microstructural barriers, hindering the nucleation and growth of microstructurally short fatigue cracks.

引用

页码：243 / 251

页数：9

共 50 条

[21] The Microstructure and Pitting Resistance of Weld Joints of 2205 Duplex Stainless Steel
Mingfang Wu
Fei Liu
Juan Pu
Neil E. Anderson
Leijun Li
Dashuang Liu
Journal of Materials Engineering and Performance, 2017, 26 : 5341 - 5347
[22] The Microstructure and Pitting Resistance of Weld Joints of 2205 Duplex Stainless Steel
Wu, Mingfang
Liu, Fei
Pu, Juan
Anderson, Neil E.
Li, Leijun
Liu, Dashuang
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2017, 26 (11) : 5341 - 5347
[23] Experimental and Numerical Investigation on Laser Welding of 2205 Duplex Stainless Steel
Ghosh A.
Misra D.
Acharyya S.K.
Lasers in Manufacturing and Materials Processing, 2019, 6 (3) : 228 - 246
[24] Weldability of a 2205 duplex stainless steel using plasma arc welding
Urena, A.
Otero, E.
Utrilla, M. V.
Munez, C. J.
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2007, 182 (1-3) : 624 - 631
[25] Induced Magnetic Field Used to Detect the Sigma Phase of a 2205 Duplex Stainless Steel
Edgard de Macedo Silva
Josinaldo Pereira Leite
João Pereira Leite
Walter Macedo Lins Fialho
Victor Hugo C. de Albuquerque
João Manuel R. S. Tavares
Journal of Nondestructive Evaluation, 2016, 35
[26] Thermal aging effect on 2205 duplex stainless steel
WANG Zhiyu
CHEN Xu
Baosteel Technical Research, 2017, 11 (03) : 24 - 29
[27] Induced Magnetic Field Used to Detect the Sigma Phase of a 2205 Duplex Stainless Steel
Silva, Edgard de Macedo
Leite, Josinaldo Pereira
Leite, Joao Pereira
Lins Fialho, Walter Macedo
de Albuquerque, Victor Hugo C.
Tavares, Joao Manuel R. S.
JOURNAL OF NONDESTRUCTIVE EVALUATION, 2016, 35 (02)
[28] Effect of metastable pitting on stress corrosion cracking in 2205 duplex stainless steel welded joints
Wang, Dengyun
Ye, Wenhui
Zhang, Houwei
Zheng, Qing
Su, Hang
Fu, Anqing
Xu, Lining
CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2024,
[29] Prediction of Flux cored arc welding process parameters effect on 2205 duplex stainless steel
Bansal Rajkumar, G.
Murugan, N.
Welding and Cutting, 2013, 12 (01): : 34 - 37
[30] Fatigue performance and microanalysis of heat treated 2205 duplex stainless steel
Stevens, KJ
MATERIALS SCIENCE AND TECHNOLOGY, 1999, 15 (08) : 903 - 908

← 1 2 3 4 5 →