Environmental stress cracking (ESC) of ABS

被引：0

作者：

Kawaguchi, T ^{[1
]}

Nishimura, H ^{[1
]}

Miwa, F ^{[1
]}

Abe, K ^{[1
]}

Kuriyama, T ^{[1
]}

Narisawa, I ^{[1
]}

机构：

[1] Osaka Gas Co Ltd, Osaka, Japan

来源：

CONFERENCE PROCEEDINGS AT ANTEC '98: PLASTICS ON MY MIND, VOLS I-3: VOL I; PROCESSING, VOL II; SPECIAL AREAS, VOL III; MATERIALS | 1998年 / 44卷

关键词：

D O I：

暂无

中图分类号：

TQ [化学工业];

学科分类号：

0817 ;

摘要：

The environmental stress cracking (ESC) of acrylonitrile-butadiene-styrene (ABS) co-polymer caused by a non-ionic surfactant (poly-oxyethylene alkylether) was studied by constant-load tensile creep tests and edge crack tension (ECT) tests. The fracture surfaces were investigated by scanning electron microscope (SEM) and the morphology of the crack tip was investigated by transmission electron microscope (TEM). It was found that the results of the creep tests performed in the non-ionic surfactant was very different from those in air. SEM images of the fracture surfaces showed that there were three different mechanisms of fracture and that specimens had a tendency to rupture by ESC when stress was small. The results of the ECT tests and the TEM images showed that the change in the mechanism of fracture was attributable to the change of morphology at the crack tip.

引用

页码：3175 / 3179

页数：5

共 50 条

[31] Environmental stress cracking - The plastic killer - Environmental stress cracking is involved with some 25% of plastic part failures
Jansen, JA
ADVANCED MATERIALS & PROCESSES, 2004, 162 (06): : 50 - 53
[32] Cracking the ABS case
Reeves Journal, 1994, 74 (12):
[33] Environmental stress cracking of polycarbonate catheter connectors
Lewis, Peter R.
ENGINEERING FAILURE ANALYSIS, 2009, 16 (06) : 1816 - 1824
[34] ENVIRONMENTAL-STRESS CRACKING AND MORPHOLOGY OF POLYETHYLENE
BANDYOPADHYAY, S
BROWN, HR
POLYMER, 1978, 19 (05) : 589 - 592
[35] Plastic failure through environmental stress cracking
Jansen, Jeffrey
Plastics Engineering, 2015, 71 (10) : 30 - 36
[36] THRESHOLD STRESS INTENSITY CONCEPT FOR ENVIRONMENTAL CRACKING
GERBERICH, WW
CHEN, YT
INTERNATIONAL JOURNAL OF FRACTURE, 1973, 9 (03) : 369 - 371
[37] THEORY OF ENVIRONMENTAL-STRESS CRACKING OF POLYETHYLENE
BROWN, HR
POLYMER, 1978, 19 (10) : 1186 - 1188
[38] The strain in the test environmental stress cracking of plastics
Wang, HT
Pan, BR
Du, QG
Li, YQ
POLYMER TESTING, 2003, 22 (02) : 125 - 128
[39] Environmental-stress cracking in DSD recyclates
Sauberlich, J
Poschet, G
KUNSTSTOFFE-PLAST EUROPE, 1999, 89 (08): : A83 - +
[40] ENVIRONMENTAL-STRESS CRACKING OF IMPACT POLYSTYRENE
BUBECK, RA
BULLETIN OF THE AMERICAN PHYSICAL SOCIETY, 1979, 24 (03): : 416 - 416

← 1 2 3 4 5 →