Improved elevated temperature cycling of LiMn2O4 spinel through the use of a composite LiF-based electrolyte

被引:58
|
作者
Sun, X [1 ]
Lee, HS [1 ]
Yang, XQ [1 ]
McBreen, J [1 ]
机构
[1] Brookhaven Natl Lab, Upton, NY 11973 USA
关键词
D O I
10.1149/1.1405036
中图分类号
O646 [电化学、电解、磁化学];
学科分类号
081704 ;
摘要
A composite electrolyte containing LiF and a tris(pentafluorophenyl)borane (TPFPB) anion complexing agent displays superior thermal and electrochemical stability compared to commercial LiPF6-based electrolytes. Severe capacity fading of a Li/LiMn2O4 cell. with a commercial LiPF6 electrolyte, was observed when cycled at 55 degreesC. The capacity fading was attributed to acidic products, from salt hydrolysis and decomposition of the solvent, which degraded LiMn2O4 electrode. The composite electrolyte containing LiF and TPFPB is not moisture sensitive and does not produce acidic species. At room temperature, the composite electrolyte shows an improvement in capacity maintenance with cycling. However, at 55 degreesC the improvement is much greater. (C) 2001 The Electrochemical Society.
引用
收藏
页码:A184 / A186
页数:3
相关论文
共 50 条
  • [21] On the capacity deterioration of spinel phase LiMn2O4 with cycling around 4 V
    Song, MY
    Ahn, DS
    SOLID STATE IONICS, 1998, 112 (1-2) : 21 - 24
  • [22] Effects of hexamethylenetetramine as an electrolyte additive on elevated temperature performance of graphite/LiMn2O4 batteries
    Zheng, Tingting
    Wang, Zhixing
    Wang, Siwu
    Li, Xinhai
    Guo, Huajun
    Peng, Wenjie
    Wang, Jiexi
    Yan, Guochun
    IONICS, 2024, 30 (07) : 3881 - 3893
  • [23] Failure mechanism and improvement of the elevated temperature cycling of LiMn2O4 compounds through the use of the LiAlxMn2-xO4-zFz solid solution
    Amatucci, GG
    Pereira, N
    Zheng, T
    Tarascon, JM
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2001, 148 (02) : A171 - A182
  • [24] Temperature effects on the electrochemical behavior of spinel LiMn2O4 in quaternary ammonium-based ionic liquid electrolyte
    Zheng, HH
    Zhang, HC
    Fu, YB
    Abe, T
    Ogumi, Z
    JOURNAL OF PHYSICAL CHEMISTRY B, 2005, 109 (28): : 13676 - 13684
  • [25] LiMn2O4 spinel and substituted cathodes
    Thackeray, Michael M.
    Amine, Khalil
    NATURE ENERGY, 2021, 6 (05) : 566 - 566
  • [26] LiMn2O4 spinel and substituted cathodes
    Michael M. Thackeray
    Khalil Amine
    Nature Energy, 2021, 6 : 566 - 566
  • [27] Enhancing the elevated temperature performance of Li/LiMn2O4 cells by reducing LiMn2O4 surface area
    Xia, YY
    Kumada, N
    Yoshio, M
    JOURNAL OF POWER SOURCES, 2000, 90 (02) : 135 - 138
  • [28] Synthesis and character of spinel LiMn2O4
    徐茶清
    田彦文
    翟玉春
    于冰
    郭兆靖
    Transactions of Nonferrous Metals Society of China, 2004, (03) : 470 - 474
  • [29] Study on modification of spinel LiMn2O4
    Han, JD
    Jin, S
    Jing, Y
    Li, W
    Jia, YZ
    CHINESE JOURNAL OF INORGANIC CHEMISTRY, 2005, 21 (02) : 237 - 240
  • [30] A Raman study of spinel LiMn2O4
    Wang, CZ
    Gong, J
    Liu, W
    Wei, YJ
    Wu, F
    Chen, G
    CHEMICAL RESEARCH IN CHINESE UNIVERSITIES, 2003, 19 (03) : 344 - 346