Encapsulation of Electron Beam Melting Produced Alloy 718 to Reduce Surface Connected Defects by Hot Isostatic Pressing

被引:12
|
作者
Zafer, Yunus Emre [1 ]
Goel, Sneha [1 ]
Ganvir, Ashish [2 ]
Jansson, Anton [3 ]
Joshi, Shrikant [1 ]
机构
[1] Univ West, Dept Engn Sci, S-46186 Trollhattan, Sweden
[2] GKN Aerosp Engine Syst AB, Res & Technol, Dept Proc Engn, S-46181 Trollhattan, Sweden
[3] Orebro Univ, Sch Sci & Engn, S-70182 Orebro, Sweden
关键词
electron beam melting; additive manufacturing; Alloy; 718; surface defects; encapsulation; coating; hot isostatic pressing; SUBSTRATE ROUGHNESS; MICROSTRUCTURAL CHARACTERISTICS; POROSITY; POSTTREATMENTS; ADHESION; BEHAVIOR;
D O I
10.3390/ma13051226
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Defects in electron beam melting (EBM) manufactured Alloy 718 are inevitable to some extent, and are of concern as they can degrade mechanical properties of the material. Therefore, EBM-manufactured Alloy 718 is typically subjected to post-treatment to improve the properties of the as-built material. Although hot isostatic pressing (HIPing) is usually employed to close the defects, it is widely known that HIPing cannot close open-to-surface defects. Therefore, in this work, a hypothesis is formulated that if the surface of the EBM-manufactured specimen is suitably coated to encapsulate the EBM-manufactured specimen, then HIPing can be effective in healing such surface-connected defects. The EBM-manufactured Alloy 718 specimens were coated by high-velocity air fuel (HVAF) spraying using Alloy 718 powder prior to HIPing to evaluate the above approach. X-ray computed tomography (XCT) analysis of the defects in the same coated sample before and after HIPing showed that some of the defects connected to the EBM specimen surface were effectively encapsulated by the coating, as they were closed after HIPing. However, some of these surface-connected defects were retained. The reason for such remnant defects is attributed to the presence of interconnected pathways between the ambient and the original as-built surface of the EBM specimen, as the specimens were not coated on all sides. These pathways were also exaggerated by the high surface roughness of the EBM material and could have provided an additional path for argon infiltration, apart from the uncoated sides, thereby hindering complete densification of the specimen during HIPing.
引用
收藏
页码:1 / 12
页数:12
相关论文
共 50 条
  • [31] Modelling of anisotropic elastic properties in alloy 718 built by electron beam melting
    Kumara, Chamara
    Deng, Dunyong
    Moverare, Johan
    Nylen, Per
    MATERIALS SCIENCE AND TECHNOLOGY, 2018, 34 (05) : 529 - 537
  • [32] Effects of Hot Isostatic Pressing on Microstructure and Mechanical Properties of Selective Laser Melted Inconel 718 Alloy in Different Directions
    Luo H.
    Li X.-Q.
    Pan C.-L.
    Zeng K.-L.
    He P.-J.
    Pan C.-M.
    Li H.-Y.
    Surface Technology, 2022, 51 (03): : 333 - 341and362
  • [33] Influence of hot isostatic pressing on microstructure, properties and deformability of selective laser melting TC4 alloy
    Yan, Tai-qi
    Chen, Bing-qing
    Ji, Xia
    Guo, Shao-qing
    CHINA FOUNDRY, 2021, 18 (04) : 389 - 396
  • [34] Influence of hot isostatic pressing on microstructure, properties and deformability of selective laser melting TC4 alloy
    Tai-qi Yan
    Bing-qing Chen
    Xia Ji
    Shao-qing Guo
    China Foundry, 2021, 18 : 389 - 396
  • [35] Oxidation Behavior of Hastelloy X Alloy Fabricated by Selective Laser Melting and Subsequent Hot Isostatic Pressing Treatment
    Wang, Hui
    Wu, Hong
    Liu, Yong
    Qiu, Wenbin
    Deng, Hao
    Zhou, Lvjun
    Chen, Longqing
    ADVANCED ENGINEERING MATERIALS, 2022, 24 (11)
  • [36] Influence of hot isostatic pressing on microstructure,properties and deformability of selective laser melting TC4 alloy
    Tai-qi Yan
    Bing-qing Chen
    Xia Ji
    Shao-qing Guo
    ChinaFoundry, 2021, 18 (04) : 389 - 396
  • [37] High temperature oxidation of IN 718 manufactured by laser beam melting and electron beam melting: Effect of surface topography
    Sanviemvongsak, Tom
    Monceau, Daniel
    Macquaire, Bruno
    CORROSION SCIENCE, 2018, 141 : 127 - 145
  • [38] Static and dynamic response of titanium alloy produced by electron beam melting
    Mirone, G.
    Barbagallo, R.
    Corallo, D.
    Di Bella, S.
    21ST EUROPEAN CONFERENCE ON FRACTURE, (ECF21), 2016, 2 : 2355 - 2366
  • [39] STRATEGIZING WITH HOT ISOSTATIC PRESSING TREATMENTS TO REDUCE POST- PROCESSING TIME OF PBF-LB INCONEL 718 PARTS SIGNIFICANTLY
    Cassese, Andrew
    Beamer, Chad
    Shipley, James
    INTERNATIONAL JOURNAL OF POWDER METALLURGY, 2025, 61 (01):
  • [40] Effect of hot isostatic pressing on the mechanical and corrosive properties of Ti-Ni alloy fabricated by selective laser melting
    Ren, Dechun
    Zhang, Lianmin
    Liu, Yujing
    Ji, Haibin
    Li, Shujun
    Jin, Wei
    Lei, Jiafeng
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2023, 26 : 4595 - 4605