Influence of Hydrogen on GBF in Very High Cycle Fatigue of High Strength Steel

被引：5
|
作者：
Zhou Chao [1 ,2 ]
Zhang Yong-jian [1 ]
Hui Wei-jun [1 ]
Wang Lei [2 ]
机构：
[1] Cent Iron & Steel Res Inst, Natl Engn Res Ctr Adv Steel Technol, Beijing 100081, Peoples R China
[2] Northeastern Univ, Fac Mat & Met Engn, Shenyang 110819, Liaoning, Peoples R China
来源：
JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL | 2013年 / 20卷 / 12期
关键词：
hydrogen; granular bright facet; very high cycle fatigue; SUBSURFACE CRACK INITIATION; CHROMIUM-BEARING STEEL; LONG-LIFE FATIGUE; GIGACYCLE FATIGUE; REGIME; MECHANISM; FAILURE; BEHAVIOR; SIZE;
D O I：
10.1016/S1006-706X(13)60221-6
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The relationship of hydrogen, GBF (granular bright facet) and very high cycle fatigue properties of high strength spring steels 60Si2CrV with three different hydrogen contents were studied using hydrogen thermal desorption analysis and ultrasonic fatigue test. The results showed that the influence of hydrogen on the relationship between fatigue life and the ratio of GBF to inclusion size [root A(GBF/)root A(INC)] was obvious, and the expression between fatigue life and root A(GBF/)root A(INC) with different hydrogen contents can also be obtained. In addition, based on the research of hydrogen VA1Nc diffusion and GBF, it was explained why the GBF cannot form below 10(6) cycles. At last, the estimated critical fatigue life of GBF formation can be expressed accurately.
引用
收藏
页码：92 / 97
页数：6
相关论文
共 50 条
  • [1] Influence of Hydrogen on GBF in Very High Cycle Fatigue of High Strength Steel
    Chao Zhou
    Yong-jian Zhang
    Wei-jun Hui
    Lei Wang
    Journal of Iron and Steel Research International, 2013, 20 : 92 - 97
  • [2] Influence of Hydrogen on GBF in Very High Cycle Fatigue of High Strength Steel
    ZHOU Chao
    ZHANG Yong-jian
    HUI Wei-jun
    WANG Lei
    Journal of Iron and Steel Research(International), 2013, 20 (12) : 92 - 97
  • [3] The influence of hydrogen on very high properties of high strength spring cycle fatigue steel
    Li, Y. D.
    Yang, Z. G.
    Liu, Y. B.
    Li, S. X.
    Li, G. Y.
    Hui, W. J.
    Weng, Y. Q.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 489 (1-2): : 373 - 379
  • [4] On the formation of GBF of high-strength steels in the very high cycle fatigue regime
    Liu, Y. B.
    Yang, Z. G.
    Li, Y. D.
    Chen, S. M.
    Li, S. X.
    Hui, W. J.
    Weng, Y. Q.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 497 (1-2): : 408 - 415
  • [5] Factors influencing the GBF size of high strength steels in the very high cycle fatigue regime
    Liu, Y. B.
    Li, S. X.
    Li, Y. D.
    Yang, Z. G.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (03): : 935 - 942
  • [6] Influence of heat treatment on fatigue strength of 50 steel in the very high cycle regime
    Enrollment and Allocation Department, Southwest Jiaotong University, Chengdu 610031, China
    不详
    Cailiao Rechuli Xuebao, 2007, 2 (81-84):
  • [7] Estimation of the size of GBF area on fracture surface for high strength steels in very high cycle fatigue regime
    Yang, Z. G.
    Li, S. X.
    Liu, Y. B.
    Li, Y. D.
    Li, G. Y.
    Hui, W. J.
    Weng, Y. Q.
    INTERNATIONAL JOURNAL OF FATIGUE, 2008, 30 (06) : 1016 - 1023
  • [8] Very High Cycle Fatigue Behavior and Thermographic Analysis of High Strength Steel
    Shao Chuang
    Bathias, Cloude
    Wagner, Daniele
    Tao Hua
    MATERIALS AND PRODUCT TECHNOLOGIES, 2010, 118-120 : 948 - +
  • [9] Very high cycle fatigue analysis of high strength steel with corrosion pitting
    Perez Mora, Ruben
    Dominguez Almaraz, Gonzalo
    Palin-Luc, Thierry
    Bathias, Claude
    Luis Arana, Jose
    FRACTURE M ECHANICS, 2010, 449 : 104 - +
  • [10] On effect of hydrogen on very high cycle fatigue behaviours of high strength steels
    Shi, J. -B.
    Li, Y. D.
    Guo, W. M.
    Xu, N.
    Wu, X. F.
    Zhao, M.
    Ma, H.
    MATERIALS SCIENCE AND TECHNOLOGY, 2013, 29 (11) : 1290 - 1296
12345