Fatigue crack propagation in austeno-ferritic duplex stainless steel 22 Cr5Ni

被引：44
|
作者：
Iacoviello, F [1 ]
Boniardi, M
La Vecchia, GM
机构：
[1] Univ Cassino, Dipartimento Meccan Strutture Ambiente & Terr, Cassino, FR, Italy
[2] Politecn Milan, Dipartimento Meccan, I-20133 Milan, Italy
[3] Univ Brescia, Dipartimento Ingn Meccan, I-25060 Brescia, Italy
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 1999年 / 21卷 / 09期
关键词：
fatigue crack propagation; duplex stainless steel; 475 degrees C embrittlement; sigma phase;
D O I：
10.1016/S0142-1123(99)00076-6
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Fatigue crack propagation in Duplex Stainless Steels (DSSs) is strongly affected by microstructure and therefore by the choice of the steel grade or by the heat treatment conditions. In the present work fatigue behaviour of 22 Cr 5 Ni DSS has been investigated both after solution annealing and after different embrittling thermal cycles. Fatigue tests have been done in air considering the influence of both the stress ratio and the loading direction. Roughness analysis has been performed to point out a relationship between fracture morphology and fatigue crack propagation data and it shows that fracture surface roughness influence on fatigue crack advancing depends on loading conditions. A scanning electron microscope (SEM) fracture surface analysis has been performed to investigate the fatigue crack propagation micro mechanisms in 22 Cr 5 Ni duplex stainless steel. (C) 1999 Published by Elsevier Science Ltd. All rights reserved.
引用
收藏
页码：957 / 963
页数：7
相关论文
共 50 条
  • [41] Corrosion fatigue crack growth inhibition of duplex stainless steel
    Ahsan, M
    Gasem, Z
    DAMAGE AND FRACTURE MECHANICS VIII: COMPUTER AIDED ASSESSMENT AND CONTROL, 2004, 14 : 59 - 68
  • [42] Effects of Ti addition on microstructure and the associated corrosion behavior of a 22Cr-5Ni duplex stainless steel
    Zhang, Jiantao
    Hu, Xiaojun
    Chou, Kuochih
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2021, 72 (07): : 1201 - 1214
  • [43] Fatigue crack propagation in austenitic stainless steel weldments
    Al-Haidary, J. T.
    Wahab, A. A.
    Salam, E. H. Abdul
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2006, 37A (11): : 3205 - 3214
  • [44] Fatigue crack propagation in austenitic stainless steel weldments
    J. T. Al-Haidary
    A. A. Wahab
    E. H. Abdul Salam
    Metallurgical and Materials Transactions A, 2006, 37 : 3205 - 3214
  • [45] A Comparative Study on the Effect of Electrode on Microstructure and Mechanical Properties of Dissimilar Welds of 2205 Austeno-Ferritic and 316L Austenitic Stainless Steel
    Verma, Jagesvar
    Taiwade, Ravindra Vasantrao
    Khatirkar, Rajesh Kisni
    Kumar, Anil
    MATERIALS TRANSACTIONS, 2016, 57 (04) : 494 - 500
  • [46] Fatigue crack nucleation at Σ3(112) boundary in a ferritic stainless steel
    Hashimoto, S
    Ikehata, H
    Kato, A
    Kato, H
    Kaneko, Y
    INTERFACE SCIENCE, 1999, 7 (02) : 159 - 171
  • [47] Preferential Fatigue Crack Nucleation at Deformation Twins in a Ferritic Stainless Steel
    Taniguchi, Tomoatsu
    Kaneko, Yoshihisa
    Hashimoto, Satoshi
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2009, 73 (12) : 930 - 937
  • [48] EFFECT OF MEAN STRESS ON HYDROGEN ASSISTED FATIGUE CRACK-PROPAGATION IN DUPLEX STAINLESS-STEEL
    MARROW, TJ
    HIPPSLEY, CA
    KING, JE
    ACTA METALLURGICA ET MATERIALIA, 1991, 39 (06): : 1367 - 1376
  • [49] INITIATION AND PROPAGATION OF FATIGUE CRACK IN NI-CR-MO MARTENSITIC STEEL IN WATER
    NAKASA, K
    TAKEI, H
    ASAMOTO, T
    TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1976, 17 (11): : 728 - 732
  • [50] Microstructural and environmental effects on fatigue crack propagation in duplex stainless steels
    Marrow, T.J.
    King, J.E.
    Fatigue and Fracture of Engineering Materials & Structures, 1994, 17 (07): : 761 - 771
12345