Enhanced fatigue crack propagation resistance of an Al-Cu-Mg alloy by artificial aging

被引：42
|
作者：
Liu Yanbin [1 ]
Liu Zhiyi [1 ]
Li Yuntao [1 ]
Xia Qinkun [1 ]
Zhou Jie [1 ]
机构：
[1] Cent S Univ, Sch Mat Sci & Engn, Changsha 410083, Peoples R China
来源：
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2008年 / 492卷 / 1-2期
关键词：
Al-Cu-Mg alloys; thermal stability; fatigue crack growth; artificial aging; GPB zone;
D O I：
10.1016/j.msea.2008.03.045
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The effect of artificial aging treatment on fatigue crack propagation (FCP) resistance of an Al-Cu-Mg alloy was investigated. It was shown that FCP rate of artificially aged alloy in the Paris region is lower than that of naturally aged alloy before and after thermal exposure. During the thermal exposure, tensile strength of artificially aged alloy remained unchanged. The results of three-dimensional atom probe (3DAP), transmission electron microscope (TEM) and differential scanning calorimeter (DSC) analysis showed that Cu-Mg co-cluster in artificially aged alloy are larger than that in natural aged alloy and can stably exist during thermal exposure. Size of Cu-Mg co-cluster was found to be the main factor influencing the thermal stability of Cu-Mg co-cluster and the FCP resistance. (C) 2008 Elsevier B.V. All rights reserved.
引用
收藏
页码：333 / 336
页数：4
相关论文
共 50 条
  • [21] A link-up resulted fatigue crack branching in Al-Cu-Mg alloy
    Lu Songsong
    Bao Rui
    Zhang Ting
    Fei Binjun
    INTERNATIONAL JOURNAL OF FATIGUE, 2016, 92 : 459 - 469
  • [22] Coupling Effect of Grain Structures and Residual Secondary Phases on Fatigue Crack Propagation Behavior in an Al-Cu-Mg Alloy
    Peng Xia
    Zhiyi Liu
    Song Bai
    Journal of Materials Engineering and Performance, 2021, 30 : 2669 - 2679
  • [23] Coupling Effect of Grain Structures and Residual Secondary Phases on Fatigue Crack Propagation Behavior in an Al-Cu-Mg Alloy
    Xia, Peng
    Liu, Zhiyi
    Bai, Song
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2021, 30 (04) : 2669 - 2679
  • [24] Enhanced fatigue crack propagation resistance in a superhigh strength Al-Zn-Mg-Cu alloy by modifying RRA treatment
    Xia, Peng
    Liu, Zhiyi
    Bai, Song
    Lu, Luqing
    Gao, Lifang
    MATERIALS CHARACTERIZATION, 2016, 118 : 438 - 445
  • [25] Precipitation process along dislocations in Al-Cu-Mg alloy during artificial aging
    Feng, Zongqiang
    Yang, Yanqing
    Huang, Bin
    Han, Ming
    Luo, Xian
    Ru, Jigang
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 528 (02): : 706 - 714
  • [26] Fatigue Crack Propagation Behavior of Al-Cu-Mg-Zr Alloy
    Zheng Ziqiao
    Sun Xiaoxu
    Chen Yuanyuan
    Wei Xiuyu
    RARE METAL MATERIALS AND ENGINEERING, 2010, 39 (06) : 975 - 979
  • [27] Effect of creep aging parameters on creep resistance behavior of Al-Cu-Mg alloy
    Wu, Xintong
    Zhan, Lihua
    Guan, Chenglong
    Yang, Xiaobo
    He, Jiayang
    MATERIALS RESEARCH EXPRESS, 2019, 6 (12):
  • [28] Optimizing strength and fatigue crack propagation resistance of in-situ TiB2/Al-Cu-Mg composite sheet
    Pu, Qingqing
    Wang, Zhiping
    Luo, Tai
    Li, Yugang
    Geng, Jiwei
    Xia, Peikang
    Li, Xianfeng
    Chen, Dong
    Wang, Hongze
    Wang, Haowei
    INTERNATIONAL JOURNAL OF FATIGUE, 2024, 179
  • [29] STRUCTURE OF AL-CU-MG ALLOY IN INITIAL STAGES OF AGING
    SHCHEGOLEVA, TV
    BUINOV, NN
    SOVIET PHYSICS CRYSTALLOGRAPHY, USSR, 1968, 12 (04): : 552 - +
  • [30] INFLUENCE OF DEFORMATION BEFORE ARTIFICIAL AGING ON PROPERTIES OF AL-CU-MG ALUMINUM-ALLOY
    MAZZINI, SG
    SCRIPTA METALLURGICA ET MATERIALIA, 1994, 31 (09): : 1127 - 1130
12345