Aging embrittlement at high temperature of 9Cr3W3Co steel and its improvement method

被引：2
|
作者：
Ma Long-teng [1 ]
Liu Zheng-dong [1 ]
Bai Yin [1 ,2 ]
机构：
[1] Cent Iron & Steel Res Inst, Inst Special Steels, Beijing 100081, Peoples R China
[2] Univ Sci & Technol Beijing, Sch Mat Sci & Engn, Beijing 100083, Peoples R China
来源：
CAILIAO GONGCHENG-JOURNAL OF MATERIALS ENGINEERING | 2019年 / 47卷 / 03期
关键词：
aging embrittlement; 9Cr3W3Co steel; W content; impact toughness; HEAT-RESISTANT STEEL; LAVES PHASE; PRECIPITATION BEHAVIOR; 9-PERCENT-CR STEEL; CREEP STRENGTH; MICROSTRUCTURE; TOUGHNESS; EVOLUTION;
D O I：
10.11868/j.issn.1001-4381.2016.001344
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The main factor that results in aging embrittlement of 9Cr3W3Co steel was investigated through microstructure observation using scanning electron microscopy (SEM). The amount of each precipitates under equilibrium state in 9Cr3W3Co steel with different W content (W content is 2. 36 %, 2. 63 %, 2. 96 % and 3. 11, mass fraction) was calculated using Thermo-Calc software. The microstructure evolution during aging was studied by transmission electron microscopy (TEM), small angle X-ray scattering (SAXS) and phase analysis method. The results show that the rapid drop of impact toughness after aging for 100h is caused by the formation of Laves phase. The mass fraction of Laves phase at equilibrium state is mainly determined by the concentration of tungsten. The steel with lower tungsten content exhibits higher impact toughness after aging for 8000h, meanwhile with the smallest size and the lowest coarsening rate of Laves phase. Thus, the aging embrittlement of 9Cr3W3Co steel can be successfully suppressed by the reduction of tungsten content.
引用
收藏
页码：139 / 146
页数：8
相关论文
共 25 条
  • [11] Causes of breakdown of creep strength in 9Cr-1.8W-0.5Mo-VNb steel
    Lee, Jae Seung
    Armaki, Hassan Ghassemi
    Maruyama, Kouichi
    Muraki, Taro
    Asahi, Hitoshi
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 428 (1-2): : 270 - 275
  • [12] Precipitation of Fe2W laves phase and modeling of its direct influence on the strength of a 12Cr-2W steel
    Li, QA
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2006, 37A (01): : 89 - 97
  • [13] [李太江 Li Taijiang], 2010, [热加工工艺, Hot Working Technology], V39, P43
  • [14] [刘俊建 Liu Junjian], 2011, [合肥工业大学学报. 自然科学版, Journal of Hefei University of Technology. Natural Science], V34, P47
  • [15] Precipitation Behavior in the Heat-Affected Zone of Boron-Added 9Cr-3W-3Co Steel During Post-Weld Heat Treatment and Creep Deformation
    Liu, Yuan
    Tsukamoto, Susumu
    Sawada, Kota
    Tabuchi, Masaaki
    Abe, Fujio
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2015, 46A (05): : 1843 - 1854
  • [16] Optimised microstructure for increased creep rupture strength of MarBN steels
    Plesiutschnig, E.
    Beal, C.
    Paul, S.
    Zeiler, G.
    Sommitsch, C.
    [J]. MATERIALS AT HIGH TEMPERATURES, 2015, 32 (03) : 318 - 322
  • [17] The role of Laves phase on microstructure evolution and creep strength of novel 9%Cr heat resistant steels
    Prat, O.
    Garcia, J.
    Rojas, D.
    Sauthoff, G.
    Inden, G.
    [J]. INTERMETALLICS, 2013, 32 : 362 - 372
  • [18] [乔瑞芳 Qiao Ruifang], 2016, [材料工程, Journal of Materials Engineering], V44, P22
  • [19] Design and characterization of microstructure evolution during creep of 12% Cr heat resistant steels
    Rojas, D.
    Garcia, J.
    Prat, O.
    Carrasco, C.
    Sauthoff, G.
    Kaysser-Pyzalla, A. R.
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (16-17): : 3864 - 3876
  • [20] ROJAS D, 2011, MAT SCI ENG A, V528
123