Characterization of marginal states in structural elements with crack-like flaws

被引：0
|
作者：
Zainullin, RS
Sharafiev, RG
Yamurov, NR
Mokrousov, SN
机构：
来源：
INDUSTRIAL LABORATORY | 1996年 / 62卷 / 11期
关键词：
D O I：
暂无
中图分类号：
TH7 [仪器、仪表];
学科分类号：
0804 ; 080401 ; 081102 ;
摘要：
Critical parameters of crack-like flaws as a function of the testing pressure are examined in various steels. The safety factor derived from the test results can be used for predicting the service life of structural elements.
引用
收藏
页码：726 / 727
页数：2
相关论文
共 50 条
  • [31] Sizing Small Crack-like Flaws through Non-ideal Part Surface Using Ultrasonic Measurement Model
    Li X.
    Sun N.
    Song Y.
    Zhang S.
    Research in Nondestructive Evaluation, 2020, 31 (03): : 147 - 163
  • [32] Identification of a crack-like flaw in an orthotropic layer
    Vatul'yan, AO
    Baranov, IV
    Guseva, IA
    RUSSIAN JOURNAL OF NONDESTRUCTIVE TESTING, 2001, 37 (10) : 718 - 722
  • [33] CRACK-LIKE CREEP CAVITATION IN A NICKEL ALUMINIDE
    SCHNEIBEL, JH
    MARTINEZ, L
    ACTA METALLURGICA, 1989, 37 (08): : 2237 - 2244
  • [34] PLASTIC STRAINS AT APICES OF CRACK-LIKE DEFECTS
    GIRENKO, VS
    KASATKIN, SB
    AUTOMATIC WELDING USSR, 1976, 29 (08): : 56 - 57
  • [35] FATIGUE ANALYSIS OF CRACK-LIKE GEOMETRICAL DISCONTINUITIES
    ROCHE, RL
    RES MECHANICA, 1990, 29 (01): : 79 - 94
  • [36] VALIDATION OF CRACK-LIKE DEFECT FATIGUE ANALYSIS
    AUTRUSSON, B
    MOULIN, D
    ACKER, D
    NUCLEAR ENGINEERING AND DESIGN, 1991, 129 (03) : 307 - 313
  • [37] Identification of a Crack-Like Flaw in an Orthotropic Layer
    A. O. Vatul'yan
    I. V. Baranov
    I. A. Guseva
    Russian Journal of Nondestructive Testing, 2001, 37 : 718 - 722
  • [38] Operation of process equipment with crack-like defects
    Valeev, S., I
    Kharlamov, I. E.
    INTERNATIONAL CONFERENCE ON MODERN TRENDS IN MANUFACTURING TECHNOLOGIES AND EQUIPMENT (ICMTMTE) 2020, 2020, 971
  • [39] Method of Evaluating the Residual Life of Structural Elements with Crack-Like Surface Defects. Report No. 1. Modeling the Growth of a Surface Fatigue Crack
    Pokrovskii, V. V.
    Tkach, Y. V.
    Ivanchenko, A. G.
    Strength of Materials, 28 (01):
  • [40] Generalized definition of "crack-like" notches to finite life and SN curve transition from "crack-like" to "blunt notch" behavior
    Ciavarella, M.
    D'Antuono, P.
    Demelio, G. P.
    ENGINEERING FRACTURE MECHANICS, 2017, 179 : 154 - 164
12345