Synthesis and Characterization of Sol-Gel Alumina Fiber by Seeding α-Alumina Through Extended Ball Milling

被引：10
|
作者：
Chandradass, J. [1 ,3 ]
Bae, Dong Sik [3 ]
Balasubramanian, M. [1 ,2 ]
机构：
[1] Indian Inst Technol, Composites Technol Ctr, Madras 600036, Tamil Nadu, India
[2] Indian Inst Technol, Dept Met & Mat Engn, Madras 600036, Tamil Nadu, India
[3] Changwon Natl Univ, Sch Nano & Adv Mat Engn, Nanopowder Proc & Synth Lab, Chang Won, Gyeongnam, South Korea
来源：
MATERIALS AND MANUFACTURING PROCESSES | 2008年 / 23卷 / 08期
关键词：
Al2O3; Fibers; Grain size; Mechanical properties; Microstructure; SEM; Sintering; Sol-gel processes; Strength; Thermal analysis; X-ray diffraction;
D O I：
10.1080/10426910802382098
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Alumina fibers were prepared by sol-gel process using alpha-Al2O3 seeded boehmite sol. The starting material used for the preparation of boehmite sol was aluminium-tri-isopropoxide. Extended ball milling of boehmite sol using alumina grinding media was carried out to incorporate nucleating seeds of alpha-Al2O3 to boehmite sol. Differential thermal analysis showed that the phase transition to alpha-Al2O3 takes place at a much lower temperature by seeding alpha-Al2O3. The presence of alpha-Al2O3 seeds decreases the sintering temperature and a relatively dense microstructure with very fine grain size is formed at 1300 degrees C. The fibers sintered at 1300 degrees C have the highest tensile strength.
引用
收藏
页码：786 / 790
页数：5
相关论文
共 50 条
  • [31] Characterization for Thermal Evolution of Boehmite Precursor and Preparation of Alumina Through a Sol-Gel Process
    Jiang Ru
    Liu Haitao
    Cheng Haifeng
    RARE METAL MATERIALS AND ENGINEERING, 2018, 47 : 188 - 192
  • [32] Structural evolution of phosphated alumina during sol-gel synthesis
    Lima, E
    Valente, J
    Bosch, P
    Lara, V
    JOURNAL OF PHYSICAL CHEMISTRY B, 2005, 109 (37): : 17435 - 17439
  • [33] Sol-gel synthesis of alumina using inorganic salt precursor
    Hao Zhi-Xian
    Liu Hui
    Guo Bin
    Li Hong
    Zhang Jia-Wei
    Gan Li-Hua
    Xu Zi-Jie
    Chen Long-Wu
    ACTA PHYSICO-CHIMICA SINICA, 2007, 23 (03) : 289 - 294
  • [34] Sol-gel synthesis of mesostructured γ-alumina templated by cationic surfactants
    Aguado, J
    Escola, JM
    Castro, MC
    Paredes, B
    MICROPOROUS AND MESOPOROUS MATERIALS, 2005, 83 (1-3) : 181 - 192
  • [35] Sol-gel synthesis of titania-alumina catalyst supports
    Kaneko, EY
    Pulcinelli, SH
    da Silva, VT
    Santilli, CV
    APPLIED CATALYSIS A-GENERAL, 2002, 235 (1-2) : 71 - 78
  • [36] Size-controlled synthesis of nano α-alumina particles through the sol-gel method
    Mirjalili, F.
    Hasmaliza, M.
    Abdullah, L. Chuah
    CERAMICS INTERNATIONAL, 2010, 36 (04) : 1253 - 1257
  • [37] Synthesis and characterization of CaO doped alumina-zirconia fibers by sol-gel process
    Chandradass, J.
    Balasubramanian, M.
    MATERIALS AND MANUFACTURING PROCESSES, 2008, 23 (02) : 159 - 162
  • [38] Sol-gel synthesis of alumina modified by phosphorus: a solid state NMR characterization study
    Quartararo, J
    Guelton, M
    Rigole, M
    Amoureux, JP
    Fernandez, C
    Grimblot, J
    JOURNAL OF MATERIALS CHEMISTRY, 1999, 9 (10) : 2637 - 2646
  • [39] Synthesis and Characterization of Alumina Powders Obtained at Various Temperatures Via Sol-Gel Method
    Attil, Hakim
    Aksas, Ali
    Sebais, Miloud
    Halimi, Ouahiba
    METALLURGICAL & MATERIALS ENGINEERING, 2024, 30 (03) : 67 - 79
  • [40] Preparation of alumina through a sol-gel process. Synthesis, characterization, thermal evolution and model of intermediate boehmite
    Nguefack, M
    Popa, AF
    Rossignol, S
    Kappenstein, C
    PHYSICAL CHEMISTRY CHEMICAL PHYSICS, 2003, 5 (19) : 4279 - 4289
12345