Preparation of a new water-based strippable protected coating

被引：3
|
作者：
Liu, Hongyu [1 ]
Zhang, Song [1 ]
机构：
[1] POB 7220, Beijing 100072, Peoples R China
来源：
ADVANCED MATERIALS, PTS 1-4 | 2011年 / 239-242卷
关键词：
water-based; strippable; coating; polyurethane; nano-CaCO3;
D O I：
10.4028/www.scientific.net/AMR.239-242.2646
中图分类号：
TQ [化学工业];
学科分类号：
0817 ;
摘要：
A new water-based strippable protected coating was made by polyurethane emulsion and nano-CaCO3 was put in the coating as the fillers. The influence of nano-CaCO3 on the coating was discussed and the influence of film thickness on the coating was studied. The performance of the coating was tested, and when the dosage of nano-CaCO3 was 2% and the film thickness was 0.13 similar to 0.14mm, the film had the best strippable ability. Its average mechanics intensity was 5.72MPa and average elongation at break was 258.35%.
引用
收藏
页码：2646 / +
页数：2
相关论文
共 50 条
  • [21] Study on Water-based High Reflectivity Insulation Coating
    Luo, Ya-fen
    Du, Zhao-qun
    Yu, Wei-dong
    ADVANCES IN TEXTILE ENGINEERING, 2011, 331 : 703 - 707
  • [22] Getting started in... Water-based conformal coating
    Anon
    EP Electronic Production (London), 2001, 30 (03):
  • [23] PRODUCTION HYGIENE IN THE MANUFACTURE OF WATER-BASED COATING MATERIALS
    JORG, R
    JOCCA-SURFACE COATINGS INTERNATIONAL, 1994, 77 (12): : 503 - 505
  • [24] Coagulation of water-based dispersions as interesting coating technique
    Blaum, Gerhard
    Unitex, 2001, (06): : 13 - 15
  • [25] Preparation and printing properties of castor oil-based UV-curable water-based coating ink
    Qi, Dongming
    Fan, Gaoqing
    Yu, Yihao
    Fu, Ye
    Zhang, Yan
    Chen, Zhijie
    Fangzhi Xuebao/Journal of Textile Research, 2022, 43 (05): : 30 - 31
  • [26] Investigation on anticorrosion performance of nano and micro polyaniline in new water-based epoxy coating
    Bagherzadeh, M. R.
    Ghasemi, M.
    Mahdavi, F.
    Shariatpanahi, H.
    PROGRESS IN ORGANIC COATINGS, 2011, 72 (03) : 348 - 352
  • [27] Preparation and properties of water-based conducting polyaniline
    Wang, XH
    Geng, YH
    Yu, L
    Sun, ZC
    Li, J
    Jing, XB
    Wang, FS
    Lee, CJ
    Rhee, SB
    CHEMICAL RESEARCH IN CHINESE UNIVERSITIES, 1998, 14 (03) : 309 - 314
  • [28] Preparation of a cellulose and water-based resin composite
    Ummartyotin, S.
    Sain, M.
    MATERIALS LETTERS, 2014, 123 : 70 - 74
  • [29] Preparation and Properties of Water-based Conducting Polyaniline
    WANG Xian hong
    Chemical Research in Chinese Universities, 1998, (03) : 87 - 92
  • [30] IMPROVED PREPARATION OF WATER-BASED CUTTING FLUIDS
    POLYANSKOV, YV
    SOVIET ENGINEERING RESEARCH, 1986, 6 (02): : 73 - 75
12345