Preparation of a new water-based strippable protected coating

被引：3
|
作者：
Liu, Hongyu [1 ]
Zhang, Song [1 ]
机构：
[1] POB 7220, Beijing 100072, Peoples R China
来源：
ADVANCED MATERIALS, PTS 1-4 | 2011年 / 239-242卷
关键词：
water-based; strippable; coating; polyurethane; nano-CaCO3;
D O I：
10.4028/www.scientific.net/AMR.239-242.2646
中图分类号：
TQ [化学工业];
学科分类号：
0817 ;
摘要：
A new water-based strippable protected coating was made by polyurethane emulsion and nano-CaCO3 was put in the coating as the fillers. The influence of nano-CaCO3 on the coating was discussed and the influence of film thickness on the coating was studied. The performance of the coating was tested, and when the dosage of nano-CaCO3 was 2% and the film thickness was 0.13 similar to 0.14mm, the film had the best strippable ability. Its average mechanics intensity was 5.72MPa and average elongation at break was 258.35%.
引用
收藏
页码：2646 / +
页数：2
相关论文
共 50 条
  • [1] Preparation of water-based anti-graffiti polyurethane coating
    Liu, Hu
    Zhu, Hongyan
    Shang, Qianqian
    Xiao, Guomin
    ADVANCES IN CHEMICAL, MATERIAL AND METALLURGICAL ENGINEERING, PTS 1-5, 2013, 634-638 : 2993 - 2996
  • [2] Using nanoemeraldine salt-polyaniline for preparation of a new anticorrosive water-based epoxy coating
    Bagherzadeh, M. R.
    Mahdavi, F.
    Ghasemi, M.
    Shariatpanahi, H.
    Faridi, H. R.
    PROGRESS IN ORGANIC COATINGS, 2010, 68 (04) : 319 - 322
  • [3] WATER-BASED COATING SYSTEMS
    BULGOZDY, EL
    INDUSTRIAL FINISHING, 1972, 48 (07): : 24 - &
  • [4] Water-based anticorrosion coating
    Cailiao Baohu, 4 (11-14):
  • [5] New Additive to Eliminate Pinholes for Water-based Coating Formulations
    Reader, Jim
    VabOosterwijk, Jos
    Xu, Caixuan
    Dai, Ye
    Mertsch, Ruediger
    McAuliffe, Shauna
    Tang, Jianchang
    COATINGSTECH, 2021, 18 (03): : 30 - 37
  • [6] Characterization and Protective Properties of a New Water-based Acryl Coating
    Drob, Silviu Iulian
    Pirvu, Cristian
    Moreno, Jose Maria Calderon
    Vasilescu, Cora
    Popa, Mihai Vasile
    REVISTA DE CHIMIE, 2013, 64 (03): : 287 - 293
  • [7] Preparation of a Novel Water-based Acrylic Multi-Thermal Insulation Coating
    Ye, Xiufang
    Chen, Dongchu
    Chang, Menglei
    Mo, Youtian
    Wang, Qingxiang
    MATERIALS SCIENCE-MEDZIAGOTYRA, 2017, 23 (02): : 173 - 179
  • [8] Water-based strippable coatings containing bentonite clay for heavy metal surface decontamination
    Toader, Gabriela
    Stanescu, Paul-Octavian
    Zecheru, Teodora
    Rotariu, Traian
    El-Ghayoury, Abdelkrim
    Teodorescu, Mircea
    ARABIAN JOURNAL OF CHEMISTRY, 2019, 12 (08) : 4026 - 4034
  • [9] Preparation of a low contact angle water-based coating using ultrasonic irradiation
    Zhang, X. R.
    Liu, L. Z.
    Li, J. F.
    Cui, W. W.
    Weng, L.
    PIGMENT & RESIN TECHNOLOGY, 2014, 43 (06) : 341 - 346
  • [10] Optimization of coating with water-based barriers
    Larsson, Tom
    Emilsson, Per
    TAPPI JOURNAL, 2019, 18 (02): : 111 - 118
12345