Fatigue behavior of polypropylene fiber reinforced concrete under constant and variable amplitude loading

被引：22
|
作者：
Mohamadi, M. R. [1 ]
Mohandesi, J. Aghazadeh [1 ]
Homayonifar, M. [1 ]
机构：
[1] Amirkabir Univ Technol, Min & Met Engn Dept, Tehran, Iran
来源：
JOURNAL OF COMPOSITE MATERIALS | 2013年 / 47卷 / 26期
关键词：
Fatigue; fiber-reinforced concrete; crack growth; variable amplitude loading; damage curve approach; LIFE PREDICTION; DAMAGE RULE; FRACTURE; RELIABILITY; PERFORMANCE; STRENGTH;
D O I：
10.1177/0021998312464083
中图分类号：
TB33 [复合材料];
学科分类号：
摘要：
In this study, fatigue behavior of polypropylene fiber reinforced concrete has been studied under constant and variable amplitude loading. Crack length was measured during flexural fatigue test under three loads. Accordingly, damage curves were determined as function of stress levels. The results ascertained that the presence of 1wt% polypropylene fibers considerably increases resistance against fatigue crack growth under constant amplitude loading. Under variable amplitude loading, it was found that the damage curve approach predicts the fatigue life with 13-15.8% estimation error, whereas linear model predicts the fatigue life with 36.8-56.5% estimation error.
引用
收藏
页码：3331 / 3342
页数：12
相关论文
共 50 条
  • [41] CONSTANT AND VARIABLE AMPLITUDE FATIGUE BEHAVIOR OF 8 STEELS
    STEPHENS, RI
    BENNER, PH
    MAURITZSON, G
    TINDALL, GW
    JOURNAL OF TESTING AND EVALUATION, 1979, 7 (02) : 68 - 81
  • [42] Deformation behavior of polypropylene fiber reinforced concrete subject to compressive fatigue loading: Averaged ε-n curve and probabilistic ultimate fatigue strain model
    Cui, Kai
    Xu, Lihua
    Chi, Yin
    COMPOSITE STRUCTURES, 2025, 357
  • [43] Fatigue failure prediction method and constant amplitude equivalence strategy of adhesive interface under variable amplitude loading
    Pan, Wenfeng
    Sun, Lingyu
    Wei, Junlei
    Zhang, Yiben
    Gao, Xinli
    Wang, Jiaxin
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2024, 129
  • [44] Numerical Analysis of Reinforced Concrete and Steel-Fiber Concrete Elements under Fatigue Loading
    Isojeh, Benard
    El-Zeghayar, Maria
    Vecchio, Frank J.
    JOURNAL OF STRUCTURAL ENGINEERING, 2019, 145 (11)
  • [45] Behavior of lightly reinforced fiber reinforced concrete panels under pure shear loading
    Facconi, Luca
    Minelli, Fausto
    ENGINEERING STRUCTURES, 2020, 202
  • [46] Experimental Investigation on Damage Behavior of Polypropylene Fiber Reinforced Concrete under Compression
    Lihua Xu
    Biao Li
    Xiaoxiao Ding
    Yin Chi
    Changning Li
    Biao Huang
    Yuchuan Shi
    International Journal of Concrete Structures and Materials, 2018, 12
  • [47] Experimental Investigation on Damage Behavior of Polypropylene Fiber Reinforced Concrete under Compression
    Xu, Lihua
    Li, Biao
    Ding, Xiaoxiao
    Chi, Yin
    Li, Changning
    Huang, Biao
    Shi, Yuchuan
    INTERNATIONAL JOURNAL OF CONCRETE STRUCTURES AND MATERIALS, 2018, 12 (01)
  • [48] Fatigue crack propagation under variable amplitude loading
    Huang, Yuhua
    Wang, Jiaren
    Dongbei Daxue Xuebao/Journal of Northeastern University, 1996, 17 (04):
  • [49] High temperature fatigue crack growth in two metals under constant and variable amplitude loading
    Månsson, T
    Skantz, J
    Nilsson, F
    INTERNATIONAL JOURNAL OF FATIGUE, 2002, 24 (11) : 1159 - 1168
  • [50] Estimating the orientation of crack initiation planes under constant and variable amplitude multiaxial fatigue loading
    Wang, Yingyu
    Susmel, Luca
    21ST EUROPEAN CONFERENCE ON FRACTURE, (ECF21), 2016, 2 : 3233 - 3239
12345