Development of TRIP-Aided Lean Duplex Stainless Steel by Twin-Roll Strip Casting and Its Deformation Mechanism

被引:46
|
作者
Zhao, Yan [1 ]
Zhang, Weina [1 ]
Liu, Xin [1 ]
Liu, Zhenyu [1 ]
Wang, Guodong [1 ]
机构
[1] Northeastern Univ, State Key Lab Rolling & Automat, Shenyang 110819, Peoples R China
来源
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 2016年 / 47A卷 / 12期
基金
中国国家自然科学基金;
关键词
TRANSFORMATION-INDUCED PLASTICITY; INDUCED MARTENSITIC-TRANSFORMATION; AUSTENITE STABILITY; EPSILON-MARTENSITE; NITROGEN-CONTENT; STRAIN-RATE; MICROSTRUCTURE; BEHAVIOR; ALLOY; SOLIDIFICATION;
D O I
10.1007/s11661-016-3771-5
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
In the present work, twin-roll strip casting was carried out to fabricate thin strip of a Mn-N alloyed lean duplex stainless steel with the composition of Fe-19Cr-6Mn-0.4N, in which internal pore defects had been effectively avoided as compared to conventional cast ingots. The solidification structure observed by optical microscope indicated that fine Widmannstatten structure and coarse-equiaxed crystals had been formed in the surface and center, respectively, with no columnar crystal structures through the surface to center of the cast strip. By applying hot rolling and cold rolling, thin sheets with the thickness of 0.5 mm were fabricated from the cast strips, and no edge cracks were formed during the rolling processes. With an annealing treatment at 1323 K (1050 A degrees C) for 5 minutes after cold rolling, the volume fractions of ferrite and austenite were measured to be approximately equal, and the distribution of alloying elements in the strip was further homogenized. The cold-rolled and annealed sheet exhibited an excellent combination of strength and ductility, with the ultimate tensile strength and elongation having been measured to be 1000 MPa and 65 pct, respectively. The microstructural evolution during deformation was investigated by XRD, EBSD, and TEM, indicating that ferrite and austenite had different deformation mechanisms. The deformation of ferrite phase was dominated by dislocation slipping, and the deformation of austenite phase was mainly controlled by martensitic transformation in the sequence of gamma ->epsilon-martensite ->alpha'-martensite, leading to the improvement of strength and plasticity by the so-called transformation-induced plasticity (TRIP) effect. By contrast, lean duplex stainless steels of Fe-21Cr-6Mn-0.5N and Fe-23Cr-7Mn-0.6N fabricated by twin-roll strip casting did not show TRIP effects and exhibited lower strength and elongation as compared to Fe-19Cr-6Mn-0.4N.
引用
收藏
页码:6292 / 6303
页数:12
相关论文
共 50 条
  • [31] DIRECT STRIP CASTING OF 18-8 STAINLESS-STEEL BY UNEQUAL DIAMETER TWIN-ROLL METHOD
    TOYAMA, N
    ABO, H
    YOSHIMURA, H
    ARAI, H
    TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1986, 26 (04) : B149 - B150
  • [32] Numerical simulation of the temperature fields of stainless steel with different roller parameters during twin-roll strip casting
    Fang, Yuan
    Wang, Zhen-min
    Yang, Qing-xiang
    Zhang, Yun-kun
    Liu, Li-gang
    Hu, Hong-yan
    Zhang, Yue
    INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2009, 16 (03) : 304 - 308
  • [33] Study of measurement and control of free loop of hot steel strip in twin-roll strip casting
    YE Changhong
    FANG Yuan
    ZHANG Qing
    BaosteelTechnicalResearch, 2018, 12 (01) : 27 - 33
  • [34] Numerical simulation and experimental research on cracking mechanism of twin-roll strip casting
    Lv, Zheng
    Yang, Zhou-Yi
    Zhang, Jian-Yu
    Li, Xue-Tong
    Ji, Peng
    Zhou, Qian
    Zhang, Xi-Liang
    Shi, Yin-Dong
    HIGH TEMPERATURE MATERIALS AND PROCESSES, 2022, 41 (01) : 694 - 701
  • [35] Effect of casting parameters on the freezing point position of the 304 stainless steel during twin-roll strip casting process by numerical simulation
    Li, Q.
    Zhang, Y. K.
    Liu, L. G.
    Zhang, P.
    Zhang, Y.
    Fang, Y.
    Yang, Q. X.
    JOURNAL OF MATERIALS SCIENCE, 2012, 47 (09) : 3953 - 3960
  • [36] Effect of casting parameters on the freezing point position of the 304 stainless steel during twin-roll strip casting process by numerical simulation
    Q. Li
    Y. K. Zhang
    L. G. Liu
    P. Zhang
    Y. Zhang
    Y. Fang
    Q. X. Yang
    Journal of Materials Science, 2012, 47 : 3953 - 3960
  • [37] A Nonlinear Dynamic Switched-Mode Model of Twin-Roll Steel Strip Casting
    Browne, Florian
    Chiu, George T. -C.
    Jain, Neera
    JOURNAL OF DYNAMIC SYSTEMS MEASUREMENT AND CONTROL-TRANSACTIONS OF THE ASME, 2019, 141 (08):
  • [38] Thin strip casting of steel with a twin-roll caster - Correlations between process parameters
    Buchner, AR
    STEEL RESEARCH, 1997, 68 (06): : 247 - 257
  • [39] A medium-Mn steel processed by novel twin-roll strip casting route
    Wang, Hesong
    Zhang, Yuanxiang
    Ran, Rong
    Wang, Yang
    Kang, Jian
    Li, Yunjie
    Misra, D. K.
    Yuan, Guo
    Wang, Guodong
    MATERIALS SCIENCE AND TECHNOLOGY, 2019, 35 (10) : 1227 - 1238
  • [40] Si-STEEL THIN-STRIP PREPARED BY TWIN-ROLL CONTINUOUS CASTING
    Yi, Yu
    Zhou, Zehua
    Wang, Zehua
    Jiang, Shaoqun
    Huang, Weidong
    SURFACE REVIEW AND LETTERS, 2011, 18 (3-4) : 97 - 102