Contact reactive brazing of Ti53311S alloy using Cu foil as interlayer: Interfacial microstructure and joining properties

被引：21
|
作者：
Song, X. G. [1 ,2 ]
Cao, J. [2 ]
Chen, H. Y. [2 ]
Wang, H. Q. [2 ]
Feng, J. C. [1 ,2 ]
机构：
[1] Harbin Inst Technol Weihai, Sch Mat Sci & Engn, Weihai 264209, Peoples R China
[2] Harbin Inst Technol, State Key Lab Adv Welding & Joining, Harbin 150001, Peoples R China
来源：
MATERIALS & DESIGN | 2013年 / 46卷
基金：
中国国家自然科学基金;
关键词：
TITANIUM-ALLOY; STRENGTH PROPERTIES; FILLER-METAL; TI-6AL-4V; C103;
D O I：
10.1016/j.matdes.2012.11.044
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Contact reactive brazing of Ti53311S alloy was extensively evaluated using Cu foil as interlayer within the range of 940-1020 degrees C for 10 min. Effect of brazing temperature on the interfacial microstructure and its evolution as well as joining properties were investigated in detail. TiCu and Ti3Cu4 intermetallic compounds formed in joint by isothermal solidification and peritectic reaction (TiCu + L -> Ti3Cu4) when the brazing temperature was 940 degrees C. A eutectoid microstructure consisting of alpha-Ti and Ti2Cu phases was produced by the eutectoid reaction (beta-Ti -> alpha-Ti + Ti2Cu) in joint when brazed at 960-1000 degrees C. Whereas when brazing was conducted at 1020 degrees C (above the alpha -> beta transus temperature 1010 degrees C), Lamellar(alpha + beta) structure was obtained in joint by isothermal solidification and subsequent phase transformation. Tensile test indicated that the maximum average tensile strength reached 932.6 MPa at room temperature. Brittle fractures were observed in all of the brazed specimens although the fracture mode was different. (C) 2012 Elsevier Ltd. All rights reserved.
引用
收藏
页码：895 / 901
页数：7
相关论文
共 50 条
  • [21] Interfacial microstructure and properties of TiAl alloy brazed joint with Ni-34Ti brazing alloy
    Song X.
    Si X.
    Ni H.
    Cao J.
    Yu J.
    Feng J.
    Cao, Jian (cao_jian@hit.edu.cn), 2017, Harbin Research Institute of Welding (38): : 13 - 16
  • [22] Interfacial microstructure and phase constitution of the Cu/Al dissimilar metals joint made by contact reactive brazing
    Zhang, Hongtao
    Cao, Jian
    Lu, Hao
    MANUFACTURING SCIENCE AND ENGINEERING, PTS 1-5, 2010, 97-101 : 3891 - +
  • [23] Brazing diamond/Cu composite to alumina using reactive Ag-Cu-Ti alloy
    Wu, Mao
    Cao, Che-zheng
    Rafi-ud-din
    He, Xin-bo
    Qu, Xuan-hui
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2013, 23 (06) : 1701 - 1708
  • [24] Interfacial segregation of Ti in the brazing of diamond grits onto a steel substrate using a Cu-Sn-Ti brazing alloy
    Li, WC
    Liang, C
    Lin, ST
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2002, 33 (07): : 2163 - 2172
  • [25] Interfacial segregation of Ti in the brazing of diamond grits onto a steel substrate using a Cu-Sn-Ti brazing alloy
    Wen-Chung Li
    Shun-Tian Lin
    Cheng Liang
    Metallurgical and Materials Transactions A, 2002, 33 : 2163 - 2172
  • [26] Brazing ZrO2 ceramic to Ti-6Al-4V alloy using NiCrSiB amorphous filler foil: Interfacial microstructure and joint properties
    Cao, J.
    Song, X. G.
    Li, C.
    Zhao, L. Y.
    Feng, J. C.
    MATERIALS CHARACTERIZATION, 2013, 81 : 85 - 91
  • [27] Joining TiB2?TiC?SiC composite to Ta with a Ti/Ni/Ti interlayer: Interfacial microstructure and mechanical properties
    Cai, Xiaoqiang
    Wang, Dongpo
    Wang, Ying
    Yang, Zhenwen
    JOURNAL OF MANUFACTURING PROCESSES, 2021, 64 : 1349 - 1358
  • [28] Joining of TiAl Alloy Using Novel Ag-Cu Sputtered Coated Ti Brazing Filler
    Simoes, Sonia
    Soares, Ana
    Tavares, Carlos Jose
    Guedes, Anibal
    MICROSCOPY AND MICROANALYSIS, 2019, 25 (01) : 192 - 195
  • [29] Joining of sintered silicon carbide using ternary Ag-Cu-Ti active brazing alloy
    Liu, Y.
    Huang, Z. R.
    Liu, X. J.
    CERAMICS INTERNATIONAL, 2009, 35 (08) : 3479 - 3484
  • [30] Interfacial microstructure and joining properties of TiAl/Ti3AlC2 diffusion bonded joints using Zr and Ni foils as interlayer
    Liu, Jiakun
    Cao, Jian
    Lin, Xingtao
    Chen, Haiyan
    Wang, Jun
    Feng, Jicai
    VACUUM, 2014, 102 : 16 - 25
12345