Surface-enhanced Raman scattering effect of gold nanoparticle arrays: The influence of annealing temperature, excitation power and array thickness

被引：9

作者：

Liu, G. Q. ^{[1
,4
]}

Liu, Z. Q. ^{[2
,3
]}

Chen, Y. H. ^{[1
,4
]}

Huang, K. ^{[1
,4
]}

Li, L. ^{[1
,4
]}

Tang, F. L. ^{[1
,4
]}

Gong, L. X. ^{[1
,4
]}

Hu, Y. ^{[1
,4
]}

Zhang, X. N. ^{[1
,4
]}

机构：

[1] Jiangxi Normal Univ, Coll Phys & Commun Elect, Nanchang 330022, Peoples R China

[2] Nanjing Univ, Dept Phys, Nanjing 210093, Jiangsu, Peoples R China

[3] Nanjing Univ, Natl Lab Solid State Microstruct, Nanjing 210093, Jiangsu, Peoples R China

[4] Key Lab Optoelect & Telecommun Jiangxi, Nanchang 330022, Peoples R China

来源：

OPTIK | 2013年 / 124卷 / 21期

基金：

中国国家自然科学基金;

关键词：

Surface-enhanced Raman scattering; Optical material and property; Metal forming and shaping; SERS;

D O I：

10.1016/j.ijleo.2013.03.048

中图分类号：

O43 [光学];

学科分类号：

070207 ; 0803 ;

摘要：

Gold nanoparticle arrays are fabricated for surface-enhanced Raman scattering (SERS) and the effect of the annealing temperature, the thickness of nanoparticle array and the exciting power on the SERS signals are investigated. The particle distribution and particle size are dense and uniform on the glass substrate when the 10 nm gold film was annealed at 250 degrees C and strong SERS signals for Rhodamine 6G were achieved via a 532 nm excitation with a 10 mW power. The SERS signal at 1650 cm(-1) is enhanced more than 10 times as compared to that of the gold film without annealing. The strong SERS behavior of gold nanoparticle arrays may broaden the SERS applications in biomedical and analytical chemistry. (C) 2013 Elsevier GmbH. All rights reserved.

引用

页码：5124 / 5126

页数：3

共 50 条

[1] Surface-enhanced Raman scattering effect of gold nanoparticle arrays: The influence of annealing temperature, excitation power and array thickness (vol 124, pg 5124, 2013)
Liu, G. Q.
Liu, Z. Q.
Chen, Y. H.
Huang, K.
Li, L.
Tang, F. L.
Gong, L. X.
Hu, Y.
Zhang, X. N.
OPTIK, 2016, 127 (07): : 3698 - 3700
[2] Optimized surface-enhanced Raman scattering on gold nanoparticle arrays
Félidj, N
Aubard, J
Lévi, G
Krenn, JR
Hohenau, A
Schider, G
Leitner, A
Aussenegg, FR
APPLIED PHYSICS LETTERS, 2003, 82 (18) : 3095 - 3097
[3] Facile fabrication of gold nanoparticle arrays for efficient surface-enhanced Raman scattering
Wang, Yuling
Chen, Hongjun
Wang, Erkang
NANOTECHNOLOGY, 2008, 19 (10)
[4] Tunable surface-enhanced Raman scattering from large gold nanoparticle arrays
Wei, A
Kim, B
Sadtler, B
Tripp, SL
CHEMPHYSCHEM, 2001, 2 (12) : 743 - +
[5] Surface-enhanced Raman scattering effect of ordered gold nanoparticle array for rhodamine B with different morphologies
Xi-hong Zu
Zhi-hui Jian
Guo-bin Yi
Hai-liang Huang
Ben-bin Zhong
Hong-sheng Luo
Jia-rong Huang
Cui Wang
Chinese Journal of Polymer Science, 2015, 33 : 1470 - 1476
[6] Surface-enhanced Raman scattering effect of ordered gold nanoparticle array for rhodamine B with different morphologies
Zu, Xi-hong
Jian, Zhi-hui
Yi, Guo-bin
Huang, Hai-liang
Zhong, Ben-bin
Luo, Hong-sheng
Huang, Jia-rong
Wang, Cui
CHINESE JOURNAL OF POLYMER SCIENCE, 2015, 33 (10) : 1470 - 1476
[7] Surface-enhanced Raman Scattering Effect of Ordered Gold Nanoparticle Array for Rhodamine B with Different Morphologies
Xi-hong Zu
Zhi-hui Jian
易国斌
Hai-liang Huang
Ben-bin Zhong
Hong-sheng Luo
Jia-rong Huang
Cui Wang
Chinese Journal of Polymer Science, 2015, 33 (10) : 1470 - 1476
[8] Aligned gold nanoneedle arrays for surface-enhanced Raman scattering
Yang, Yong
Tanemura, Masaki
Huang, Zhengren
Jiang, Dongliang
Li, Zhi-Yuan
Huang, Ying-ping
Kawamura, Go
Yamaguchi, Kohei
Nogami, Masayuki
NANOTECHNOLOGY, 2010, 21 (32)
[9] An effective surface-enhanced Raman scattering template based on gold nanoparticle/silicon nanowire arrays
王明利
张常兴
吴正龙
井西利
许海军
Chinese Physics B, 2014, 23 (06) : 551 - 557
[10] An effective surface-enhanced Raman scattering template based on gold nanoparticle/silicon nanowire arrays
Wang Ming-Li
Zhang Chang-Xing
Wu Zheng-Long
Jing Xi-Li
Xu Hai-Jun
CHINESE PHYSICS B, 2014, 23 (06)

← 1 2 3 4 5 →