PHYSICAL AND CHEMICAL SIMULATION OF THE THAUMASITE FORM OF SULFATE ATTACK ON CONCRETE

被引：0

作者：

Ma, Baoguo ^{[1
]}

Luo, Zhongtao ^{[1
]}

Li, Xiangguo ^{[1
]}

Gao, Xiaojian

Wang, Kai ^{[1
]}

机构：

[1] Wuhan Univ Technol, Key Lab Silicate Mat Sci & Engn, Minist Educ, Wuhan, Peoples R China

来源：

MICROSTRUCTURE RELATED DURABILITY OF CEMENTITIOUS COMPOSITES, VOLS 1 AND 2 | 2008年 / 61卷

关键词：

D O I：

暂无

中图分类号：

TB33 [复合材料];

学科分类号：

摘要：

The transformation of physical and chemical performance was studied in the thaumasite form of sulfate attack (TSA) process on cement mortars, A physical and chemical simulation of TSA process was established, and the mechanism of thaumasite formation is further discussed. The visual appearance, linear deformation, mass loss and strength were tested at different storage times, and then the analysis towards the physical transformation in TSA process was carried on. X-ray diffractometer, Fourier transform infrared spectrometer and other modern testing technologies were used to analyze the chemical transformation in the TSA process. The macroscopical peculiarity due to the TSA process included corrosions from surface to inside. Gray mud Without any strength appeared on the surface, and strength loss inside mortars. When the corrosion time arrived at 450(th) day, the FTIR results of mortars' surface showed the characteristic peak value Of SiO6 (501cm(-1)), and confirm the thaumasite formation. The physical process of TSA could be disparted to 3 periods: delitescence, expansion and crack period and intenerated and disaggregating period; the chemical process of TSA could be disparted to 4 periods: ionic migration period, ettringite formation period, gypsum formation period and thaumasite formation period.

引用

页码：1093 / +

页数：3

共 50 条

[21] C, O and S isotopic signatures thaumasite formation and limited in concrete which have suffered thaumasite form of sulfate attack
Iden, IK
Hagelia, P
CEMENT & CONCRETE COMPOSITES, 2003, 25 (08): : 839 - 846
[22] Effects of superfine fly ash on thaumasite form of sulfate attack
Wu M.
Ji Y.-S.
Chen X.-F.
Zhang L.-L.
Chen X.-D.
Ji, Yong-Sheng (jysbh@126.com), 1600, Zhejiang University (50): : 1479 - 1485
[23] Thaumasite form of sulfate attack (TSA) in limestone cement pastes
Tsivilis, S.
Sotiriadis, K.
Skaropoulou, A.
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2007, 27 (2-3) : 1711 - 1714
[24] Rate of the thaumasite form of sulfate attack under laboratory conditions
Brueckner, R.
Williamson, S. J.
Clark, L. A.
CEMENT & CONCRETE COMPOSITES, 2012, 34 (03): : 365 - 369
[25] Thaumasite sulfate attack on concrete: Mechanisms, influential factors and mitigation
Rahman, M. M.
Bassuoni, M. T.
CONSTRUCTION AND BUILDING MATERIALS, 2014, 73 : 652 - 662
[26] Use of mineral admixtures to improve the resistance of limestone cement concrete against thaumasite form of sulfate attack
Skaropoulou, A.
Sotiriadis, K.
Kakali, G.
Tsivilis, S.
CEMENT & CONCRETE COMPOSITES, 2013, 37 : 267 - 275
[27] Thaumasite from of sulfate attack
Concrete (London), 2 (37):
[28] Estimation of the Occurrence Time of Thaumasite Sulfate Attack on Tunnel Lining Concrete
Xu, Chongbang
Gao, Xiaojing
Li, Xuefeng
Zhang, Kaishun
ADVANCES IN CIVIL ENGINEERING, 2020, 2020
[29] Chemical and Physical Sulfate Attack on Fly Ash Concrete Mixtures
Dhole, Rajaram
Thomas, Michael D. A.
Folliard, Kevin J.
Drimalas, Thano
ACI MATERIALS JOURNAL, 2019, 116 (04) : 31 - 42
[30] Mechanism and Preventive Technology of the Thaumasite Form of Sulfate Attack on Cement Mortars
马保国
Journal of Wuhan University of Technology-Materials Science Edition, 2006, (S1) : 27 - 30

← 1 2 3 4 5 →