Preparation of nanosheet Fe-ZSM-5 catalysts, and effect of Fe content on acidity, water, and sulfur resistance in the selective catalytic reduction of NO x by ammonia

被引：22
|
作者：
Ma, Luoning [1 ]
Qu, Hongxia [1 ]
Zhang, Jie [1 ]
Tang, Qisheng [1 ]
Zhang, Shule [1 ]
Zhong, Qin [1 ]
机构：
[1] Nanjing Univ Sci & Technol, Sch Chem Engn, Nanjing 210094, Jiangsu, Peoples R China
来源：
RESEARCH ON CHEMICAL INTERMEDIATES | 2013年 / 39卷 / 09期
基金：
中国国家自然科学基金;
关键词：
Fe-ZSM-5; catalysts; Nanosheets; SCR; NOx; Water and sulfur resistance; NITRIC-OXIDE; ZEOLITE; NH3; TEMPERATURE; OXIDATION; FEZSM-5; MFI; NITROGEN; SITES; N2O;
D O I：
10.1007/s11164-012-0927-9
中图分类号：
O6 [化学];
学科分类号：
0703 ;
摘要：
Direct synthesis of nanosheet Fe-ZSM-5 catalysts and their use for selective catalytic reduction (SCR) of NO (x) by ammonia were studied. XRD, BET, SEM, EPR, and NH3-TPD were used to understand the properties of catalysts with different iron loading. XRD confirmed the presence of the ZSM-5 crystal phase, and there was no Fe2O3 phase on the surface of the crystals. SEM showed the Fe-ZSM-5 catalysts comprised microspheres made up of nanosheets. EPR indicated that the iron was present as isolated Fe(3+)and FeO (x) oligomers uniformly dispersed throughout the crystals. NH3-TPD indicated that Fe-ZSM-5 (20,1:1) had maximum acid sites and density at approximately 250 and 450 A degrees C, respectively. Fe-ZSM-5 (20,1:1) had the highest activity in the SCR reaction with NH3. It was also confirmed that Fe-ZSM-5 (20,1:1) had excellent resistance to SO2 and H2O under the SCR reaction conditions. The effects of water vapor and SO2, iron loading, and the Si/(Fe + Al) ratio were also investigated for these catalysts.
引用
收藏
页码：4109 / 4120
页数：12
相关论文
共 50 条
  • [21] Selective catalytic reduction of NO with ammonia over Fe promoted Mo/ZSM-5 catalysts
    Li Zhe
    Chen Bing
    Huang Wei
    Xie Ke-Chang
    CHEMICAL JOURNAL OF CHINESE UNIVERSITIES-CHINESE, 2006, 27 (10): : 1907 - 1911
  • [22] Catalytic wet oxidation of phenol with Fe-ZSM-5 catalysts
    Yan, Ying
    Jiang, Songshan
    Zhang, Huiping
    RSC ADVANCES, 2016, 6 (05) : 3850 - 3859
  • [23] NITROUS OXIDE CATALYTIC DECOMPOSITION OVER FE-ZSM-5 CATALYSTS: EFFECT OF ALUMINUM AND IRON CONTENT
    Cardona, E.
    Rios, L.
    Pena, J.
    INGENIERIA QUIMICA, 2010, (38): : 38 - 45
  • [24] Active sites for NO reduction over Fe-ZSM-5 catalysts
    Schwidder, M
    Kumar, MS
    Brückner, A
    Grünert, W
    CHEMICAL COMMUNICATIONS, 2005, (06) : 805 - 807
  • [25] Effect of Preparation Procedure on the Catalytic Properties of Fe-ZSM-5 as SCR Catalyst
    Shishkin, Alexander
    Carlsson, Per-Anders
    Harelind, Hanna
    Skoglundh, Magnus
    TOPICS IN CATALYSIS, 2013, 56 (9-10) : 567 - 575
  • [26] Kinetics of selective catalytic reduction of NO with NH3 on Fe-ZSM-5 catalyst
    Huang, HY
    Long, RQ
    Yang, RT
    APPLIED CATALYSIS A-GENERAL, 2002, 235 (1-2) : 241 - 251
  • [27] Effect of Preparation Procedure on the Catalytic Properties of Fe-ZSM-5 as SCR Catalyst
    Alexander Shishkin
    Per-Anders Carlsson
    Hanna Härelind
    Magnus Skoglundh
    Topics in Catalysis, 2013, 56 : 567 - 575
  • [28] Fe-ZSM-5 for Selective Catalytic Reduction of NO with NH3: A Comparative Study of Different Preparation Techniques
    R.Q. Long
    R.T. Yang
    Catalysis Letters, 2001, 74 : 201 - 205
  • [29] Fe-ZSM-5 for selective catalytic reduction of NO with NH3:: a comparative study of different preparation techniques
    Long, RQ
    Yang, RT
    CATALYSIS LETTERS, 2001, 74 (3-4) : 201 - 205
  • [30] Selective catalytic reduction of NOx with ammonia over Fe-Mo/ZSM-5 catalysts
    Li, Z
    Xie, KC
    Huang, XW
    Reschetilowski, W
    CHEMICAL ENGINEERING & TECHNOLOGY, 2005, 28 (07) : 797 - 801
12345