Impregnation and drying schedule of Eucalyptus wood

The aim of this research was to define a rapid and simple test that would indicate the probable performance of a pretreated wood species in a hot-press drying process and the kiln schedule. The drying rate (mass/time) and the remaining mass of water were measured at different moisture intervals. The moisture of timber decreased rapidly and the drying rate was 3.7% per day in the early five days. The timbers were B grade after drying used the hot-press drying kiln in 16 days. The moisture content of timber reached 9.20% after the drying process with the standard deviation of 0.92%. The gradient of the moisture content was 3.40%. The moisture content standard deviation in the thickness of timber was 2.70% and the residual stress was 1.38%. The mechanical properties of impregnation wood improve significantly compared to the untreated wood. The basic density of impregnation wood improved by 17.1%, the over-dried density increased to 0.55 g.cm(-3) from 0.49 g.cm(-3). The scanning electron microscopy explained the wood modifier has been permeated into the wood fiber which reacted with the wood composition.