Toughness Scatter About FCAW-S Girth Weld for X80 Pipeline Steel

被引：0
|
作者：
Xu, Youxiao [1 ]
Wang, Feng [2 ]
Chen, Lin [1 ]
Wei, Ziyun [1 ]
Song, Weichen [1 ]
机构：
[1] Sinopec Petr Engn Co Ltd, 49 Jinnan Rd, Yingkou 257026, Peoples R China
[2] China Petr Pipeline Res Inst Co Ltd, 44 Jinguang Rd, Langfang 065000, Peoples R China
来源：
ADVANCES IN MATERIALS PROCESSING | 2018年
关键词：
X80; pipeline; Flux-Cored arc welding self; Girth weld; Toughness scatter; MA constituent; HEAT-AFFECTED ZONE; MICROSTRUCTURE; FRACTURE;
D O I：
10.1007/978-981-13-0107-0_101
中图分类号：
TM [电工技术]; TN [电子技术、通信技术];
学科分类号：
0808 ; 0809 ;
摘要：
The toughness scatter about Flux-Cored Arc Welding Self for X80 pipeline steel was investigated to explore the reason that causes toughness scatter, and how to improve the toughness scatter. The type of the metallography, the volume fraction and the pattern distribution of M/A constituents, and the effects of them to the weld toughness were studied by weld thermal-cycle curves measurement, thermal simulation experiments, Charpy Impact Test, optical microscope observation and SEM. The results showed that the toughness scatter was observed in temperature region of A(c1)-A(c3), MA constituent directly related to the charpy impact toughness, toughness decreased with increasing of the volume fraction of MA constituent. It is considered that bacilliform MA is the main reason that cause toughness scatter, bulk MA is another reason that cause low toughness.
引用
收藏
页码：1065 / 1074
页数：10
相关论文
共 50 条
  • [31] Simulation Analysis of the Strain Behaviour of X80 Girth Weld Joint
    Wang, Shixin
    Li, Zhiwen
    Li, Zhenglong
    Zhang, Zhaojun
    Han, Changchai
    ADVANCES IN MATERIALS PROCESSING, 2018, : 1055 - 1063
  • [32] INVESTIGATION ON MECHANICAL PROPERTIES OF X80 PIPELINE GIRTH WELD WELDED BY SEMI-AUTOMATIC AND AUTOMATIC WELDING
    Ren, Wei
    Shuai, Jian
    PROCEEDINGS OF ASME 2022 PRESSURE VESSELS AND PIPING CONFERENCE, PVP2022, VOL 4B, 2022,
  • [33] Enhancing the Toughness of Heavy thick X80 Pipeline Steel Plates By Microstructure Control
    Nie, Wenjin
    Xin, Weifeng
    Xu, Tianming
    Shi, Peijian
    Zhang, Xiaobing
    ADVANCED ENGINEERING MATERIALS, PTS 1-3, 2011, 194-196 : 1183 - 1191
  • [34] Study on fracture toughness of X80 pipeline steel based on small punch test
    Cao Y.
    Wu Z.
    Si W.
    Zhen Y.
    Song M.
    Li X.
    Jiang Y.
    Zhongguo Shiyou Daxue Xuebao (Ziran Kexue Ban)/Journal of China University of Petroleum (Edition of Natural Science), 2020, 44 (05): : 131 - 138
  • [35] QUANTIFICATION OF SPLITTING IN X80 PIPELINE STEEL
    Gervasyev, Alexey
    Petrov, Roumen
    Pyshmintsev, Igor
    Huo, Chunyong
    Barbaro, Frank
    PROCEEDINGS OF THE 12TH INTERNATIONAL PIPELINE CONFERENCE, 2018, VOL 3, 2018,
  • [36] Hydrogen diffusion simulation of the X80 pipeline steel girth weld zone considering the synergistic effect of the structure-stress-concentration field
    Xu, Taolong
    Guo, Sihan
    Fu, Bangwen
    Ma, Xiaoling
    Han, Haoyu
    Li, Youlv
    Jiang, Hongye
    ENGINEERING FAILURE ANALYSIS, 2024, 160
  • [37] EXPERIMENTAL STUDY ON GIRTH WELDS OF X80 HIGH DEFORMABILITY PIPELINE
    He, Xiaodong
    Huo, Chunyong
    Han, Xinli
    Zhu, Lixia
    Zhuang, Chuanjing
    PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE - 2008, VOL 6, PT A AND B, 2009, : 349 - 352
  • [38] Influence of H2S Corrosion on Tensile Properties and Fracture Toughness of X80 Pipeline Steel
    L. Gu
    J. Wang
    C. B. Luan
    X. Y. Li
    Strength of Materials, 2019, 51 : 145 - 155
  • [39] INFLUENCE OF H2S CORROSION ON TENSILE PROPERTIES AND FRACTURE TOUGHNESS OF X80 PIPELINE STEEL
    Gu, L.
    Wang, J.
    Luan, C. B.
    Li, X. Y.
    STRENGTH OF MATERIALS, 2019, 51 (01) : 145 - 155
  • [40] Effect of H2S Corrosion on the Fracture Toughness of the X80 Pipeline Steel Welded Joint
    Wang, Xueli
    Wang, Dongpo
    Deng, Caiyan
    Li, Chengning
    MATERIALS, 2022, 15 (13)
12345