Preparation and properties of electrochromic iridium oxide thin film by sol-gel process

被引：76
|
作者：
Nishio, K [1 ]
Watanabe, Y [1 ]
Tsuchiya, T [1 ]
机构：
[1] Sci Univ Tokyo, Fac Ind Sci & Technol, Dept Mat Sci & Technol, Noda, Chiba 2788510, Japan
来源：
THIN SOLID FILMS | 1999年 / 350卷 / 1-2期
关键词：
sol-gel process; electrical properties and measurements; iridium; optical properties; oxides;
D O I：
10.1016/S0040-6090(99)00290-4
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
We established a method for preparation of iridium oxide thin film by the sol-gel dip-coating process where iridium chloride was used as a starting material. The coating solution was prepared by reacting iridium chloride, ethanol and acetic acid. Iridium oxide coating was formed at 2.0 cm/min withdrawing rate. The coating films heat treated at 300 degrees C did not contain impurities. Iridium oxide crystallized at temperatures above 450 degrees C. Both crystalline and amorphous iridium oxide thin films showed electrochromism. The change in transmittance of the crystalline Ir2O3 film is larger than that of the amorphous Ir2O3 under the same experimental conditions. The transmittance of the crystalline thin firm (film thickness 200 nm, measured at 400 nm) decreased 13.0% on application of 3 V for 1 s. (C) 1999 Elsevier Science S.A. All rights reserved.
引用
收藏
页码：96 / 100
页数：5
相关论文
共 50 条
  • [31] Characterization and preparation of ITO thin film from hydrothermal and sol-gel process
    Zhi, Li
    Xu, Hua-Rui
    Zhou, Huai-Ying
    Gongneng Cailiao/Journal of Functional Materials, 2006, 37 (SUPPL.): : 237 - 238
  • [32] Alcohol sensing of tin oxide thin film prepared by sol-gel process
    Sunita Mishra
    C. Ghanshyam
    Nathai Ram
    Satinder Singh
    R. P. Bajpai
    R. K. Bedi
    Bulletin of Materials Science, 2002, 25 : 231 - 234
  • [33] Tungsten and Titanium Oxide Thin Films Obtained by the Sol-Gel Process as Electrodes in Electrochromic Devices
    Rizzuto, Carmen
    Barberi, Riccardo C.
    Castriota, Marco
    FRONTIERS IN MATERIALS, 2022, 9
  • [34] Alcohol sensing of tin oxide thin film prepared by sol-gel process
    Mishra, S
    Ghanshyam, C
    Ram, N
    Singh, S
    Bajpai, RP
    Bedi, RK
    BULLETIN OF MATERIALS SCIENCE, 2002, 25 (03) : 231 - 234
  • [35] Optical, spectroelectrochemical and structural properties of sol-gel derived Ni-oxide electrochromic film
    Surca, A
    Orel, B
    Pihlar, B
    Bukovec, P
    JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 1996, 408 (1-2) : 83 - 100
  • [36] Preparation of Lithium Titanate Thin Film for Electrochromic Smart Window by Sol-Gel Spin Coating Method
    Wang Tianyue
    Wang Mengying
    Huang Qingjiao
    Yang Jiaming
    Wang Shunhua
    Diao Xungang
    JOURNAL OF INORGANIC MATERIALS, 2021, 36 (05) : 471 - 478
  • [37] Preparation of ZnO thin film by sol-gel method and its photocatalytic properties
    School of Physics Science and Technology, Central South University, Changsha 410083, China
    不详
    不详
    Nami Jishu yu Jingmi Gongcheng/Nanotechnology and Precision Engineering, 2008, 6 (02): : 94 - 98
  • [38] Preparation of Lithium Titanate Thin Film for Electrochromic Smart Window by Sol-Gel Spin Coating Method
    Wang, Tianyue
    Wang, Mengying
    Huang, Qingjiao
    Yang, Jiaming
    Wang, Shunhua
    Diao, Xungang
    Wuji Cailiao Xuebao/Journal of Inorganic Materials, 2021, 36 (05): : 471 - 478
  • [39] Electrochromic and electrochemical properties of nickel oxide thin films prepared by a modified sol-gel method
    Xia, X. H.
    Tu, J. P.
    Zhang, J.
    Wang, X. L.
    MULTI-FUNCTIONAL MATERIALS AND STRUCTURES, PTS 1 AND 2, 2008, 47-50 : 625 - 629
  • [40] Preparation of titanium(IV) oxide thin film photocatalyst by sol-gel dip coating
    Sonawane, RS
    Hegde, SG
    Dongare, MK
    MATERIALS CHEMISTRY AND PHYSICS, 2003, 77 (03) : 744 - 750
12345