Low-temperature ordering of L10 FePt by PtMn underlayer

被引：49

作者：

Chiang, CC ^{[1
]}

Lai, CH ^{[1
]}

Wu, YC ^{[1
]}

机构：

[1] Natl Tsing Hua Univ, Dept Mat Sci & Engn, Hsinchu 300, Taiwan

来源：

APPLIED PHYSICS LETTERS | 2006年 / 88卷 / 15期

关键词：

D O I：

10.1063/1.2191422

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

The ordering temperature of FePt films grown on PtMn underlayers was reduced due to phase transformation of the PtMn L1(0) phase. The in-plane coercivity of 10 nm FePt on 50 nm PtMn underlayers was 7688 Oe after annealing at 325 degrees C. An exchange field of 554 Oe was also observed, which indicates that PtMn may not only induce the ordering of FePt at a reduced temperature, but also may provide extra anisotropy. A large coercivity of 10500 Oe can be achieved for 35 nm FePt films on PtMn underlayers after 325 degrees C annealing.

引用

页数：3

共 50 条

[31] L10 FePt films epitaxially grown on MgO substrates with or without a Cr underlayer
Ding, Y. F.
Chen, J. S.
Liu, E.
Li, L.
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2006, 303 (02) : E238 - E242
[32] Effect of composition on L10 ordering in FePt and FePtCu thin films
Li, BH
Feng, C
Yang, T
Teng, J
Zhai, ZH
Yu, GH
Zhu, FW
JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2006, 39 (06) : 1018 - 1021
[33] Ordering of island-like FePt L10 thin films
Kim, MG
Shin, SC
Kang, KH
APPLIED PHYSICS LETTERS, 2002, 80 (20) : 3802 - 3804
[34] L10 FePt: Ordering, Anisotropy Constant and Their Relation to Film Composition
Barmak, Katayun
Wang, Bincheng
Jesanis, Andrew T.
Berry, David C.
Rickman, Jeffrey M.
IEEE TRANSACTIONS ON MAGNETICS, 2013, 49 (07) : 3284 - 3291
[35] Low-temperature fabrication of high-coercivity L10 ordered FePt magnetic thin films by sputtering
Takahashi, YK
Ohnuma, M
Hono, K
JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS, 2001, 40 (12B): : L1367 - L1369
[36] Low-temperature fabrication of high-coercivity L10 ordered FePt magnetic thin films by sputtering
Takahashi, Y.K.
Ohnuma, M.
Hono, K.
2001, Japan Society of Applied Physics (40):
[37] Evolution of stress with L10 ordering in FePt and FeCuPt thin films
Wierman, KW
Platt, CL
Howard, JK
Spada, FE
JOURNAL OF APPLIED PHYSICS, 2003, 93 (10) : 7160 - 7162
[38] Preparation of L10 ordered CuAu buffer layer and its effect on the L10 ordering in the FePt thin film
Chen, J
Ishio, S
Sugawara, S
THIN SOLID FILMS, 2003, 426 (1-2) : 211 - 215
[39] Reduction of the fcc to L10 ordering temperature for self-assembled FePt nanoparticles containing Ag
Kang, S
Harrell, JW
Nikles, DE
NANO LETTERS, 2002, 2 (10) : 1033 - 1036
[40] Controlling the crystallographic orientation in ultrathin L10 FePt (111) films on MgO(111) underlayer
Jeong, JY
Kim, JG
Bae, SY
Shin, KH
IEEE TRANSACTIONS ON MAGNETICS, 2001, 37 (04) : 1268 - 1270

← 1 2 3 4 5 →