New criterion of fatigue fracture initiation and crack growth model in pearlitic steels

被引：0
|
作者：
Karzov, GP
Margolin, BZ
Shvetsova, VA
机构：
来源：
ECF 11 - MECHANISMS AND MECHANICS OF DAMAGE AND FAILURE, VOLS I-III | 1996年
关键词：
D O I：
暂无
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Strain-power criterion of fatigue fracture initiation is formulated for bcc-metals, in particular, for perlitic steels on the base of some physical and mechanical ideas about damage cumulation under cyclic loading. Fatigue crack growth model which allow to describe the crack path and rate into inhomogeneous stress field at various stress ratio factors is proposed.
引用
收藏
页码：1137 / 1142
页数：6
相关论文
共 50 条
  • [41] Fatigue Crack Initiation and Growth (Supplement).
    Glinka, Grzegorz
    Politechnika Warszawska, Prace Naukowe, Mechanika, 1982, (79): : 5 - 42
  • [42] A FURTHER STUDY ON FATIGUE CRACK INITIATION LIFE - MECHANICAL MODEL FOR FATIGUE CRACK INITIATION
    ZHENG, X
    INTERNATIONAL JOURNAL OF FATIGUE, 1986, 8 (01) : 17 - 21
  • [43] On the mesoscale fracture initiation criterion of heterogeneous steels during quenching
    Said Schicchi D.
    Caggiano A.
    Lübben T.
    Hunkel M.
    Hoffmann F.
    Materials Performance and Characterization, 2017, 6 (01) : 80 - 104
  • [44] Ultimate exhaustion of local plasticity as a criterion of fatigue crack initiation
    G. V. Tsybanev
    A. I. Novikov
    Strength of Materials, 2010, 42 : 101 - 107
  • [45] CRITERION FOR ANALYSING FATIGUE CRACK INITIATION IN GEOMETRICAL SINGULARITIES.
    Devaux, J.C.
    D'Escatha, Y.
    Rabbe, P.
    Pellissier-Tanon, A.
    Transactions of the International Conference on Structural Mechanics in Reactor Technology, 1979, G.
  • [46] ULTIMATE EXHAUSTION OF LOCAL PLASTICITY AS A CRITERION OF FATIGUE CRACK INITIATION
    Tsybanev, G. V.
    Novikov, A. I.
    STRENGTH OF MATERIALS, 2010, 42 (01) : 101 - 107
  • [47] A DISLOCATION MODEL FOR FATIGUE CRACK INITIATION
    TANAKA, K
    MURA, T
    JOURNAL OF APPLIED MECHANICS-TRANSACTIONS OF THE ASME, 1981, 48 (01): : 97 - 103
  • [48] A DISLOCATION MODEL FOR FATIGUE CRACK INITIATION
    VENKATARAMAN, G
    NAKASONE, Y
    MURA, T
    CHUNG, YW
    JOURNAL OF METALS, 1988, 40 (11): : 90 - 90
  • [49] CRACK INITIATION, SLOW CRACK-GROWTH, AND UNSTABLE PROPAGATION OF DUCTILE FRACTURE IN MILD STEELS IN A LABORATORY EXPERIMENT
    OGASAWARA, M
    KURIYAMA, Y
    TAMANO, T
    MIMURA, H
    YANAGIMOTO, S
    JOURNAL OF TESTING AND EVALUATION, 1981, 9 (05) : 296 - 302
  • [50] A new fatigue crack growth mechanism of high-strength steels
    Li, H. F.
    Zhang, P.
    Zhang, Z. F.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2022, 840
12345