Effect of laser shock processing on sulfide stress corrosion cracking of X70 pipeline steel welded joint

被引：0

作者：

Pei, Junfeng ^{[1
]}

Liu, Junning ^{[1
]}

He, Weiying ^{[1
]}

机构：

[1] Changzhou Univ, Coll Mech & Energy Engn, Changzhou 213016, Peoples R China

来源：

FRONTIERS OF MANUFACTURING AND DESIGN SCIENCE, PTS 1-4 | 2011年 / 44-47卷

关键词：

Laser shock processing; Sulfide stress corrosion cracking; X70 welded joint; ACIDIC SOIL ENVIRONMENT; RESIDUAL-STRESSES; BEHAVIOR; ALLOY;

D O I：

10.4028/www.scientific.net/AMM.44-47.451

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Laser shock processing (LSP) is a new technique for metal surface strengthening by which residual compressive stress in the superficial layer can be induced to greatly improve the stress corrosion resistance property. The effect of LSP on sulfide stress corrosion cracking (SSCC) of X70 pipeline steel welded joint has been studied in this paper. A convergent lens is used to deliver 20 J, 20 ns laser pulses by a Q switch Nd:YAG laser, operating at 10 Hz. The pulses are focused to a diameter of 3 mm onto samples. The power density of laser at the surface of the sample was about 5 GW/cm2. The surface residual stress level after LSP is much higher than before. SSCC behavior of X70 pipeline steel welded joint was investigated using slow strain rate testing (SSRT) in H2S solution. Morphology of X70 pipeline steel fracture surface was observed by scanning electron microscope (SEM). It has been demonstrated that LSP is an effective surface treatment technique to improve the stress corrosion cracking (SCC) resistance properties of X70 pipeline steel welded joints.

引用

页码：451 / 455

页数：5

共 50 条

[21] Effect off deteriorated microstructures on stress corrosion cracking of X70 pipeline steel in acidic soil environment
Liu, Zhiyong
Zhai, Guoli
Li, Xiaogang
Du, Cuiwei
JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING, 2008, 15 (06): : 707 - 713
[22] Corrosion and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in a CO2-Containing Solution
L. Zhang
X.G. Li
C.W. Du
Y.F. Cheng
Journal of Materials Engineering and Performance, 2009, 18 : 319 - 323
[23] Corrosion and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in a CO2-Containing Solution
Zhang, L.
Li, X. G.
Du, C. W.
Cheng, Y. F.
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2009, 18 (03) : 319 - 323
[24] Effect of hydrogen-induced plasticity on the stress corrosion cracking of X70 pipeline steel in simulated soil environments
Liu, Z. Y.
Wang, X. Z.
Du, C. W.
Li, J. K.
Li, X. G.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 658 : 348 - 354
[25] Effect of Dissolved Oxygen on Stress Corrosion Cracking of X70 Pipeline Steel in Near-Neutral pH Solution
Liu, Z. Y.
Li, X. G.
Du, C. W.
Wang, L. X.
Huang, Y. Z.
CORROSION, 2010, 66 (01)
[26] Effect of pH Value on the Electrochemical and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in the Dilute Bicarbonate Solutions
Cui, Z. Y.
Liu, Z. Y.
Wang, L. W.
Ma, H. C.
Du, C. W.
Li, X. G.
Wang, X.
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2015, 24 (11) : 4400 - 4408
[27] Effect of pH Value on the Electrochemical and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in the Dilute Bicarbonate Solutions
Z. Y. Cui
Z. Y. Liu
L. W. Wang
H. C. Ma
C. W. Du
X. G. Li
X. Wang
Journal of Materials Engineering and Performance, 2015, 24 : 4400 - 4408
[28] Understanding the effect of tensile stress on erosion-corrosion of X70 pipeline steel
Wang, Weizhi
Hu, Junying
Yuan, Xi
Zhou, Li
Yu, Jiansheng
Zhang, Zhi
Zhong, Xiankang
CONSTRUCTION AND BUILDING MATERIALS, 2022, 342
[29] Study on the microstructure and hardness of in-service welded joint of X70 pipeline steel
陈玉华
王勇
刘鸽平
China Welding, 2007, (04) : 68 - 71
[30] Electrochemical mechanism of stress corrosion cracking of API X70 pipeline steel under different AC frequencies
Liu, Q.
Wu, W.
Pan, Y.
Liu, Z. Y.
Zhou, X. C.
Li, X. G.
CONSTRUCTION AND BUILDING MATERIALS, 2018, 171 : 622 - 633

← 1 2 3 4 5 →