Preparation of Corundum/Mullite Composites by sintering

被引：0
|
作者：
Yang, Zhongzheng [1 ]
Li, Keliang [1 ]
Zhao, Wenxuan [1 ]
Zhang, Yue [1 ]
机构：
[1] N China Univ Water Conservancy & Elect Power, Key Lab Mat, Zhengzhou 450011, Peoples R China
来源：
GREEN POWER, MATERIALS AND MANUFACTURING TECHNOLOGY AND APPLICATIONS, PTS 1 AND 2 | 2011年 / 84-85卷
关键词：
Bauxite; mullite/corundum; composites; sintering; MULLITE REFRACTORY MATERIALS; MECHANICAL-PROPERTIES; ALUMINA; BEHAVIOR; CERAMICS; WEAR;
D O I：
10.4028/www.scientific.net/AMM.84-85.64
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Mullite/corundum composites synthetized by sintering with bauxite as raw material was researched. The sintering temperature, main crystal phase, microstructure and fracture mode of the composites synthetized by sintering are different with change of ratio of Al2O3 and SiO2 and content of Al2O3: (1) If the ratio of Al2O3 and SiO2 and content of Al2O3 is low, sintering temperature of the composites is high, the main crystal phase is mullite, microstructure shows interlocking network structure formed by columnar mullite, the fracture mode of composites shows that mullite appears in the pulled out state; (2) If the ratio of Al2O3 and SiO2 content of Al2O3 is high, sintering temperature of the composites is low, the main crystal phase is corundum, microstructure shows the skeleton structure formed by granulous corundumthe, the fracture mode of composites shows intergranular fracture formed by corundum, occasionally transcrystalline fracture. The major reason of different sintering temperature of the composites is concerned with mullitization degree and content of glass phase.
引用
收藏
页码：64 / 68
页数：5
相关论文
共 50 条
  • [31] Development of a Mullite-Corundum Mortar for Cementing Mullite-Corundum Components
    L. A. Babkina
    V. I. Drozd
    I. V. Khonchik
    V. L. Zinchenko
    L. N. Nikulina
    N. A. Stepanyuk
    Refractories and Industrial Ceramics, 2001, 42 : 372 - 373
  • [32] Development of a mullite-corundum mortar for cementing mullite-corundum components
    Babkina, LA
    Drozd, VI
    Khonchik, IV
    Zinchenko, VL
    Nikulina, LN
    Stepanyuk, NA
    REFRACTORIES AND INDUSTRIAL CERAMICS, 2001, 42 (9-10) : 372 - 373
  • [33] PREPARATION OF PRECURSOR POWDERS OF CORDIERITE-MULLITE COMPOSITES FROM METAL ALKOXIDES AND ITS SINTERING
    SUZUKI, H
    SAITO, H
    NIPPON SERAMIKKUSU KYOKAI GAKUJUTSU RONBUNSHI-JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 1988, 96 (06): : 659 - 665
  • [34] Mechanical Properties of Mullite-Corundum Composites Prepared from Bauxite
    Maldhure, Atul V.
    Tripathi, Himansu S.
    Ghosh, Arup
    INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2015, 12 (04) : 860 - 866
  • [35] Densification and sintering behavior of mullite-zirconia and mullite-ceria composites
    Bozano, DF
    Neves, PP
    ADVANCED POWDER TECHNOLOGY, 1999, 299-3 : 149 - 156
  • [36] Sintering behavior and microstructure of SiAlON bonded corundum composites in different sintering atmospheres
    Hubei Province Key Lab. of Ceramics and Refractories, Wuhan University of Science and Technology, Wuhan 430081, China
    Naihao Cailiao, 2006, 1 (4-8):
  • [37] Mullite/β-spodumene composites: Preparation and characterization
    Naga, S. M.
    El-Maghraby, A. A.
    Hassan, A. M.
    CERAMICS INTERNATIONAL, 2016, 42 (10) : 12161 - 12166
  • [38] Reaction sintering of kyanite and alumina to form mullite composites
    Goski, DG
    Caley, WF
    CANADIAN METALLURGICAL QUARTERLY, 1999, 38 (02) : 119 - 126
  • [39] Effects of sintering temperature on pore characterization and strength of porous corundum-mullite ceramics
    Yan, Wen
    Li, Nan
    Han, Bingqiang
    JOURNAL OF CERAMIC PROCESSING RESEARCH, 2010, 11 (03): : 388 - 391
  • [40] Fabrication of mullite composites by cyclic infiltration and reaction sintering
    Lin, Yung-Jen
    Chen, Yi-Chi
    Materials Science and Engineering: A, 2001, 298 (1-2) : 179 - 186
12345