Influence of CaO Addition, FeO/SiO2, and MgO/SiO2 on the Melting Characteristic Temperatures of FeO-SiO2 -MgO-CaO System

被引：0
|
作者：
Ma, Yongbo [1 ,2 ]
Du, Xueyan [1 ,2 ]
机构：
[1] Lanzhou Univ Technol, Sch Mat Sci & Engn, Lanzhou 730050, Gansu, Peoples R China
[2] Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Gansu, Peoples R China
来源：
MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS | 2019年 / 22卷 / 03期
关键词：
melting characteristic temperature; nickel slag; FeO/SiO2; MgO/SiO2; w(CaO);
D O I：
10.1590/1980-5373-MR-2018-0645
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In order to decrease the oxidation temperature of fayalite in molten nickel slags, the influence of CaO addition, FeO/SiO2, and MgO/SiO2 on melting characteristic temperatures of FeO-SiO2-MgO-CaO system were investigated. The melting characteristic temperatures, including softening temperature (T-s), hemispherical temperature (T-h), and flow temperature (T-f), were measured with hot stage microscope. Experimental results showed that the melting characteristic temperatures first decreased sharply and then increased slowly with increasing w(CaO) for samples at given FeO/SiO2 and MgO/SiO2 ratios. The melting characteristic temperatures of samples without CaO addition were much higher than that of samples with different CaO addition, which was mainly caused by the phase components at different compositions. The variation of melting characteristic temperatures were described in detail. Phase components and liquid fractions were calculated by FactSage 7.1, which was good agreement with the XRD patterns.
引用
收藏
页数：8
相关论文
共 50 条
  • [41] MgO Saturation Analisys of CaO-SiO2-FeO-MgO-Al2O3 Slag System
    Montecinos de Almeida, Rodolfo Arnaldo
    Vieira, Deisi
    Bielefeldt, Wagner Viana
    Faria Vilela, Antonio Cezar
    MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS, 2018, 21 (01):
  • [42] Dissolution Behavior of SiO2 into Molten CaO-FeO Phase
    Miki, Takahiro
    Kawakami, Akito
    ISIJ INTERNATIONAL, 2020, 60 (07) : 1434 - 1437
  • [43] THE STUDY ON THE INTERFACE REACTION CHARACTERISTICS OF DIFFERENT BINARY SLAG, CaO - MgO, Al2O3 - CaO, Al2O3 MgO, SiO2 - CaO, SiO2 - MgO
    Yin, R. R.
    He, Z. J.
    Qiu, S.
    Liu, J. H.
    Tian, C.
    Yuan, Y. Q.
    Zhang, J. H.
    METALURGIJA, 2019, 58 (1-2): : 15 - 18
  • [44] Dissolution behavior of SiO2 into molten CaO-FeO phase
    Miki T.
    Kawakami A.
    ISIJ International, 2020, 60 (07): : 1434 - 1437
  • [45] Influence of Atmosphere and Basicity on Softening and Melting Behaviors of the CaO-FeO-SiO2-Al2O3-MgO System
    Ueda, Shigeru
    Miki, Takahiro
    Kim, Sun-Joong
    Gao, Xu
    Nogami, Hiroshi
    Kitamura, Shin-ya
    ISIJ INTERNATIONAL, 2020, 60 (07) : 1380 - 1388
  • [46] Rate of 2CaO•SiO2 Dissolution into Molten CaO-FeO-SiO2 Slag Saturated with Solid Iron
    Kobayashi, Yoshinao
    Sadamoto, Takahide
    ISIJ INTERNATIONAL, 2017, 57 (10) : 1703 - 1709
  • [47] INTERDIFFUSIVITY OF CAO-FEO IN THE LIQUID CAO-FEO-SIO2 SYSTEM
    KISHIMOTO, M
    FUJII, S
    MORI, K
    KAWAI, Y
    TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1984, 25 (03): : 197 - 204
  • [48] THE SYSTEM CAO-MGO-FEO-SIO2 .1. PRELIMINARY DATA ON THE JOIN CASIO3-MGO-FEO
    SCHAIRER, JF
    OSBORN, EF
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1950, 33 (05) : 160 - 167
  • [49] THE OLIVINE CLINOPYROXENE GEOBAROMETER - EXPERIMENTAL RESULTS IN THE CAO-FEO-MGO-SIO2 SYSTEM
    ADAMS, GE
    BISHOP, FC
    CONTRIBUTIONS TO MINERALOGY AND PETROLOGY, 1986, 94 (02) : 230 - 237
  • [50] Effects of Basicity and FeO Content on the Softening and Melting Temperatures of the CaO-SiO2-MgO-Al2O3 Slag System
    Chuang, Hsin-Chien
    Hwang, Weng-Sing
    Liu, Shih-Hsien
    MATERIALS TRANSACTIONS, 2009, 50 (06) : 1448 - 1456
12345