One-step production of N-O-P-S co-doped porous carbon from bean worms for supercapacitors with high performance

In recent years, multi-heteroatom-doped hierarchical porous carbons (HPCs) derived from natural potential precursors and synthesized in a simple, efficient and environmentally friendly manner have received extensive attention in many critical technology applications. Herein, bean worms (BWs), a pest in bean fields, were innovatively employed as a precursorviaa one-step method to prepare N-O-P-S co-doped porous carbon materials. The pore structure and surface elemental composition of carbon can be modified by adjusting KOH dosage, exhibiting a high surface area (S-BET) of 1967.1 m(2)g(-1)together with many surface functional groups. The BW-based electrodes for supercapacitors were shown to have a good capacitance of up to 371.8 F g(-1)in 6 M KOH electrolyte at 0.1 A g(-1), and good rate properties with 190 F g(-1)at a high current density of 10 A g(-1). Furthermore, a symmetric supercapacitor based on the optimal carbon material (BWPC1/3) was also assembled with a wide voltage window of 2.0 V, demonstrating satisfactory energy density (27.5 W h kg(-1)at 200 W kg(-1)) and electrochemical cycling stability (97.1% retention at 10 A g(-1)over 10 000 charge/discharge cycles). The facile strategy proposed in this work provides an attractive way to achieve high-efficiency and scalable production of biomass-derived HPCs for energy storage.