Failure analysis of a petrochemical plant reducing gear

被引：10

作者：

Griza, Sandro ^{[1
]}

Santos, Antonio Pereira ^{[1
]}

Azevedo, Thiago Figueiredo ^{[1
]}

Fortis Kwietniewski, Carlos Eduardo ^{[2
]}

Reguly, Afonso ^{[2
]}

Strohaecker, Telmo R. ^{[2
]}

机构：

[1] Univ Fed Sergipe, Programa Posgrad Ciencia & Engn Mat, Sao Cristovao, Brazil

[2] Univ Fed Rio Grande do Sul, Programa Posgrad Engn Met Minas & Mat, Porto Alegre, RS, Brazil

来源：

ENGINEERING FAILURE ANALYSIS | 2013年 / 29卷

关键词：

Fracture mechanics; Fatigue; Crack growth; Stress concentration; Gear; COMPUTATIONAL MODEL; FATIGUE FAILURES; BENDING FATIGUE;

D O I：

10.1016/j.engfailanal.2012.11.013

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

This study aims to investigate the cause of failure of an 845 mm external diameter reducing gear that operated during 30 months in a petrochemical plant. The failure analysis procedure included material characterisation (microstructure, chemical composition and microhardness), fracture surface evaluation, and stress distribution by finite elements on critical regions of the gear. Fracture mechanics and fatigue crack growth were also used to develop a da/dN-triangle K curve and then determine the gear material crack growth resistance. Results indicate that the gear was not properly manufactured and failure occurred as a result of a fatigue process facilitated by a manufacturing defect. (c) 2012 Elsevier Ltd. All rights reserved.

引用

页码：56 / 61

页数：6

共 50 条

[41] Modal and Vibration Analysis of Filter System in Petrochemical Plant
Liu, Zhongchi
Wang, Ji
Gho, Wie Min
Liu, Xiao
Yu, Xuebing
SHOCK AND VIBRATION, 2017, 2017
[42] Tribological failure analysis of gear contacts of Exciter Sieve gear boxes
Thakre, Gananath D.
Sharma, Satish C.
Harsha, S. P.
Tyagi, M. R.
ENGINEERING FAILURE ANALYSIS, 2014, 36 : 75 - 91
[43] Fracture failure analysis of transmission gear shaft in a bidirectional gear pump
Qin Xiaofeng
Liu Jie
Zhao Xingguo
Feng Li
Pang Ruiqiang
ENGINEERING FAILURE ANALYSIS, 2020, 118 (118)
[44] Stress relaxation cracking failure in heat exchanger connection pipes in a petrochemical plant
Mallick, Ritesh Kumar
Ghosh, Manojit
Bahrami, Abbas
Esmaeili, Vahid
ENGINEERING FAILURE ANALYSIS, 2023, 147
[45] Early Detection of Gear Failure by Vibration Analysis
Merzoug, Mustapha
Ait-Sghir, Khalid
Miloudi, Abdelhamid
Dron, Jean Paul
Bolaers, Fabrice
MULTIPHYSICS MODELLING AND SIMULATION FOR SYSTEMS DESIGN AND MONITORING, 2015, 2 : 69 - 79
[46] Reinforced polymer gear: Fatigue and failure analysis
Senthilvelan, S
Gnanamoorthy, R
TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2005, 58 (2-3) : 249 - 253
[47] Failure analysis of a tandem mill ring gear
Fantin, Luiza de Brito
Moreira, Marcelo Ferreira
Moreira, Anna Ramus
ENGINEERING FAILURE ANALYSIS, 2023, 151
[48] Failure Analysis of Transmission Gear for Heavy Vehicles
Wang, Tie
Zhao, Fuqiang
Shen, Jun
ADVANCES IN POWER TRANSMISSION SCIENCE AND TECHNOLOGY, 2011, 86 : 206 - 209
[49] Failure analysis of a nose landing gear fork
Infante, V.
Fernandes, L.
Freitas, M.
Baptista, R.
ENGINEERING FAILURE ANALYSIS, 2017, 82 : 554 - 565
[50] Failure analysis of a civil aircraft landing gear
Ossa, EA
ENGINEERING FAILURE ANALYSIS, 2006, 13 (07) : 1177 - 1183

← 1 2 3 4 5 →