High-temperature mechanical behavior of Al-Cu matrix composites containing diboride particles

An aluminum-copper matrix composite reinforced with aluminum diboride particles was studied at high temperature via thermomechanometry experiments. The matrix contained 2 wt% Cu, whereas the amount of boron forming AlB2 ranged from 0 to 4 wt%, i.e., 0 to 8.31 vol% of diboride particles. In the first segment of the research, we demonstrated that larger amounts of AlB2 particles raised the composite hardness even at 300 degrees C. To assess the material creep behavior, another set of specimens were tested under 1 N compression at 400 degrees C and 500 degrees C for 12 h. Higher levels of AlB2 allowed the composites to withstand compression creep deformations at those temperatures. By using existing creep models developed for metal matrix composites we were able to determine that viscous slip deformation was the dominant deformation mechanism for the temperatures and stress levels used in our experiments. Additionally, the computed creep activation energy for these aluminum matrix composites were found comparable to the energies reported for other similar materials, for instance, Al/SiCp composites.