Features of Fracture and Fatigue Durability of the Maintained Steel of Disks of the Steam Turbine of Thermal Power Station

被引：0
|
作者：
Tkachuk, Yu. M. [1 ]
Student, O. Z.
机构：
[1] Lutsk Natl Tech Univ, UA-43018 Lutsk, Ukraine
来源：
METALLOFIZIKA I NOVEISHIE TEKHNOLOGII | 2011年 / 33卷
关键词：
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
As shown, the regulated values of mechanical properties under tension of the 34XH3M steel after operation during at congruent to 3.10(5) h as a disk of steam turbine is not satisfied that indicates on the steel degradation. As revealed, using fractography analysis, the nucleation of crack in the damaged disk of steam turbine appears by the mechanism of fretting fatigue due to low-amplitude displacements of blade roots into the disk groove, and its subsequent extension takes place by the mechanism of corrosion-fatigue crack growth. The characteristics of the high-cycle, corrosion and fretting fatigues of steels in a virgin state and after operation are compared. Salient features of fractures of such steels are revealed.
引用
收藏
页码：449 / 460
页数：12
相关论文
共 50 条
  • [31] Study on thermal fatigue fracture characteristics of a cast steel for wheel
    He, Qingfu
    Song, Zhikun
    Kang T'ieh/Iron and Steel (Peking), 2002, 37 (12): : 50 - 52
  • [32] IMPROVEMENT OF THE THERMODYNAMIC CYCLE OF STEAM TURBINE INSTALLATIONS OF THERMAL POWER PLANTS
    Lavrenchenko, Georg K.
    Slinko, Alexey G.
    Kozlovskyi, Serhii V.
    Boychuk, Artem S.
    JOURNAL OF CHEMISTRY AND TECHNOLOGIES, 2024, 32 (02): : 498 - 508
  • [33] Failure analysis in a steam turbine stop valve of a thermal power plant
    Jalali, A.
    Delouei, Amin Amiri
    ENGINEERING FAILURE ANALYSIS, 2019, 105 : 1131 - 1140
  • [34] Data reconciliation for the overall thermal system of a steam turbine power plant
    Guo, Sisi
    Liu, Pei
    Li, Zheng
    APPLIED ENERGY, 2016, 165 : 1037 - 1051
  • [35] Experience gained at the Ural Turbine Works with retrofitting steam turbine units for thermal power stations
    Valamin A.E.
    Kultyshev A.Yu.
    Gol'Dberg A.A.
    Shibaev T.L.
    Paneque Aguilera H.C.
    Thermal Engineering, 2013, 60 (8) : 541 - 547
  • [36] Fatigue fracture failure analysis of 12Cr12Mo steam turbine blade
    He, Qiqi
    Xue, Song
    He, Hongmei
    Hu, Fengtao
    Gao, HongChen
    Hu, Wei
    ENGINEERING FAILURE ANALYSIS, 2023, 150
  • [37] Creep-fatigue defect development and risk of brittle fracture in the ultrasupercritical steam turbine rotors
    Banaszkiewicz, Mariusz
    Badur, Janusz
    MATERIALS AT HIGH TEMPERATURES, 2023, 40 (01) : 1 - 12
  • [38] Design features of a 300MW nuclear power plant steam turbine
    Gao, Shu-qiang
    Li, Yuan-xi
    Dongli Gongcheng/Power Engineering, 1988, 8 (06): : 1 - 7
  • [39] A STEAM-TURBINE - GAS-TURBINE HEAT AND POWER-STATION WITH GASIFICATION OF SOLID FUEL WITHIN THE CYCLE
    VARVARSKII, VS
    GRIBOV, VB
    PRUTKOVSKII, EN
    SAVIN, VI
    THERMAL ENGINEERING, 1981, 28 (08) : 444 - 448
  • [40] Design and Simulation of SOFC and Steam Turbine based Integrated Power Plant at Ashuganj Power Station Company Limited
    Al Mamun, Khandakar Abdulla
    Islam, Naeemul
    Raju, Ekramul Haider
    Abir, Shadman Aousaf
    Zaman, Md Anis Uz
    Ahmed, Shafait
    2019 5TH INTERNATIONAL CONFERENCE ON ADVANCES IN ELECTRICAL ENGINEERING (ICAEE), 2019, : 269 - 274
12345