Synthesis of High Concentration Colloid Solution of Silica-Coated AgI Nanoparticles

Methods for high concentration silica-coated silver iodide (AgI/SiO2) particles, which could be practically used as X-ray contrast agent, were examined. The first was a single-step method, which was to prepare AgI nanoparticles at an AgI concentration of 5 x 10(-3) M and coat the AgI nanoparticles with silica shell by a Stober method. The second was a multiple-step method, which was to repeat a step for preparing a AgI/SiO2 particle colloid solution with 10(-3) M AgI 5 times for adjusting a final AgI concentration to 5 x 10(-3) M. In the two methods, dominant particle aggregation took place, though core-shell particles were also produced. The third was a salting-out method, which was to salt out AgI/SiO2 particles in their colloid solution prepared at an AgI concentration of 10(-3) M, remove supernatant by decantation, and redisperse the particles in a fresh solvent. Consequently, AgI/SiO2 particles with an AgI concentration as high as 0.05 M were successfully prepared with the salting-out method, and their core shell structure was not damaged during the salting-out.