Melt spinning of Ni-12.5 wt.%Al alloy

被引：1

作者：

Torkar, M ^{[1
]}

Sustarsic, B ^{[1
]}

机构：

[1] INST MET & TECHNOL,LJUBLJANA 1000,SLOVENIA

来源：

MATERIALS AND MANUFACTURING PROCESSES | 1997年 / 12卷 / 03期

关键词：

D O I：

10.1080/10426919708935154

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Melt spinner has been used for fabrication of Ni3Al alloy (Ni-12.5 wt.% Al) ribbon. The optimal speed of wheel during melt spinning was 20.5 m s(-1). The thickness of the ribbon was between 14 and 60 mu m and width 2 mm. During melt spinning some powder appeared as a by-product, dependent on the speed of copper wheel. Morphology of the ribbon and powder was observed. Ribbon tensile strength of up to 937 N mm(-2) and reduction of area up to 20% was measured.

引用

页码：409 / 416

页数：8

共 50 条

[21] Hot ductility of an Al-4 wt.%Mg-0.5 wt.%Cu alloy
Katholieke Universiteit Leuven, Leuven, Belgium
Mater Sci Eng A Struct Mater Prop Microstruct Process, 2 (189-196):
[22] Thermal-rate treatment and structure transformation of Al-13 wt.% Si alloy melt
Bian, XF
Wang, WM
MATERIALS LETTERS, 2000, 44 (01) : 54 - 58
[23] The microstructure of a Mg-10 wt.%Al alloy
Braszczynska, KN
ZEITSCHRIFT FUR METALLKUNDE, 2002, 93 (08): : 845 - 850
[24] Solute distribution analysis in directionally solidified Al-5.7 wt.% Ni eutectic alloy
Shetty, MN
Bansal, V
ZEITSCHRIFT FUR METALLKUNDE, 1998, 89 (01): : 42 - 46
[25] The effects of neutron irradiation on oxidation behavior, microstructure and transformation temperatures of Cu-12.7 wt.% Al-5 wt.% Ni-2 wt.% - Mn shape memory alloy
Tatar, C
Zengin, R
THERMOCHIMICA ACTA, 2005, 433 (1-2) : 56 - 58
[26] Kinetics of Fe-30% Ni-12.5% Co invar alloy during high temperature oxidation
Bong-Seo Kim
Yung-Geol Kim
Hee-Woong Lee
Won-Sub Chung
Metals and Materials International, 2002, 8 : 367 - 373
[27] Kinetics of Fe-30%Ni-12.5%Co invar alloy during high temperature oxidation
Kim, BS
Kim, BG
Lee, HW
Chung, WS
METALS AND MATERIALS INTERNATIONAL, 2002, 8 (04): : 367 - 373
[28] Investigation of trace elements in an Al-4.8 wt.% Mg-0.3 wt.% Mn alloy
Simensen, CJ
Södervall, U
SURFACE AND INTERFACE ANALYSIS, 2000, 30 (01) : 309 - 314
[29] Influence of plasma arc melting on melt structure and solidification microstructure of Al-16 wt.% Si alloy
Pan, XM
Bian, XF
Zhao, C
Sun, JQ
ALUMINUM ALLOYS 2002: THEIR PHYSICAL AND MECHANICAL PROPERTIES PTS 1-3, 2002, 396-4 : 119 - 124
[30] Simultaneous Increase of Electrical Conductivity and Hardness of Al-1.5 wt.% Mn Alloy by Addition of 1.5 wt.% Cu and 0.5 wt.% Zr
Belov, Nikolay
Korotkova, Natalya
Akopyan, Torgom
Tsydenov, Kirill
METALS, 2019, 9 (12)

← 1 2 3 4 5 →