Melt spinning of Ni-12.5 wt.%Al alloy

被引：1

作者：

Torkar, M ^{[1
]}

Sustarsic, B ^{[1
]}

机构：

[1] INST MET & TECHNOL,LJUBLJANA 1000,SLOVENIA

来源：

MATERIALS AND MANUFACTURING PROCESSES | 1997年 / 12卷 / 03期

关键词：

D O I：

10.1080/10426919708935154

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Melt spinner has been used for fabrication of Ni3Al alloy (Ni-12.5 wt.% Al) ribbon. The optimal speed of wheel during melt spinning was 20.5 m s(-1). The thickness of the ribbon was between 14 and 60 mu m and width 2 mm. During melt spinning some powder appeared as a by-product, dependent on the speed of copper wheel. Morphology of the ribbon and powder was observed. Ribbon tensile strength of up to 937 N mm(-2) and reduction of area up to 20% was measured.

引用

页码：409 / 416

页数：8

共 50 条

[1] THE DECOMPOSITION OF A NI-12.5 AT -PERCENT SI ALLOY
EPPERSON, JE
MILDNER, DFR
CHEN, H
AIP CONFERENCE PROCEEDINGS, 1982, (89) : 392 - 394
[2] Microstructure and physical properties of melt spun Al-17 wt.% Ni-10 wt.% Cu alloy
Ahmed, Emad M.
Gouda, El Said
EUROPEAN PHYSICAL JOURNAL-APPLIED PHYSICS, 2010, 50 (02): : 213011 - 213013
[3] AL-12.5WT-PERCENT SI RIBBONS PREPARED BY MELT SPINNING
BASTAWROS, AM
SAID, MZ
JOURNAL OF MATERIALS SCIENCE, 1993, 28 (05) : 1143 - 1146
[4] EARLY STAGE DECOMPOSITION OF A NI-12.5 AT -PERCENT SI ALLOY
DVORACK, MA
CHEN, H
EPPERSON, JE
JOURNAL OF METALS, 1982, 35 (12): : A47 - A48
[5] PHASE-SEPARATION IN AN NI-12.5 AT-PERCENT-AL ALLOY AT 575-K
EPPERSON, JE
LIN, JS
LABARBE, PD
JOURNAL OF APPLIED CRYSTALLOGRAPHY, 1988, 21 : 873 - 877
[6] Rapidly solidified Al-6.5 wt.% Ni alloy
Gögebakan, M
Uzun, O
Karaaslan, T
Keskin, M
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2003, 142 (01) : 87 - 92
[7] Modification effect of Ni-38 wt.%Si on Al-12 wt.%Si alloy
Wu Yuying
Liu Xiangfa
Jiang Binggang
Huang Chuanzhen
JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 477 (1-2) : 118 - 122
[8] Morphological characteristic of the conventional and melt-spun Al-10Ni-5.6Cu (in wt.%) alloy
Karakose, Ercan
Keskin, Mustafa
MATERIALS CHARACTERIZATION, 2009, 60 (12) : 1569 - 1577
[9] Nanometric AlNi Precipitation in a 84.68 wt.% Cu-11.25 wt.%Al-4.07 wt.%Ni Shape Memory Alloy
Hamouda, K.
Chentouf, S. M.
Bouabdallah, M.
Cheniti, H.
Amimer, N.
DIFFUSION IN SOLIDS AND LIQUIDS VIII, 2013, 334-335 : 1 - +
[10] Stable phase formation in a 85.67 wt.% Cu-9.9 wt.% Al-4.43 wt.% Ni shape memory alloy
Chentouf, S. M.
Bouabdallah, M.
Cheniti, H.
Keddam, M.
ESOMAT 2009 - 8TH EUROPEAN SYMPOSIUM ON MARTENSITIC TRANSFORMATIONS, 2009,

← 1 2 3 4 5 →