Failure analysis of dissimilar thickness resistance spot welded joints in dual-phase steels during tensile shear test

被引：40
|
作者：
Zhang, Hongqiang [1 ]
Qiu, Xiaoming [1 ]
Xing, Fei [1 ]
Bai, Jie [1 ]
Chen, Jianhe [2 ]
机构：
[1] Jilin Univ, Key Lab Automobile Mat, Minist Educ, Sch Mat Sci & Engn, Changchun 130025, Peoples R China
[2] Sanyou Automobile Parts Mfg Co Ltd, Changchun 130022, Peoples R China
来源：
MATERIALS & DESIGN | 2014年 / 55卷
关键词：
Ferrous metals and alloys; Welding; Fracture; MECHANICAL PERFORMANCE; MODE TRANSITION; DP600; MICROSTRUCTURE; SINGLE; SIZE;
D O I：
10.1016/j.matdes.2013.09.040
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Investigating the failure mode and failure mechanism of the dissimilar thickness dual phase sheets resistance spot welding joints was the objective of this study. Three distinct failure modes were observed during the tensile shear test: interfacial, partial interfacial and pullout failure. The results of the stress analysis of welded joints show that the tensile stress leads to the interfacial failure and the shear stress leads to the pullout failure. Due to more serious stress concentration and heat affected zone (HAZ) softening of DP780 side, the fracture is initiated from the DP780 steel. (C) 2013 Elsevier Ltd. All rights reserved.
引用
收藏
页码：366 / 372
页数：7
相关论文
共 50 条
  • [21] Microstructure and fatigue properties of fiber laser welded dissimilar joints between high strength low alloy and dual-phase steels
    Parkes, D.
    Xu, W.
    Westerbaan, D.
    Nayak, S. S.
    Zhou, Y.
    Goodwin, F.
    Bhole, S.
    Chen, D. L.
    MATERIALS & DESIGN, 2013, 51 : 665 - 675
  • [22] Mechanical and Fatigue Behavior of Resistance Spot Welded Dual-Phase and Twinning-Induced Plasticity Steel Joints
    Doruk, Emre
    Findik, Fehim
    Pakdil, Murat
    JOURNAL OF AEROSPACE ENGINEERING, 2022, 35 (03)
  • [23] Characteristics of electrode wear in resistance spot welding dual-phase steels
    Zhang, X. Q.
    Chen, G. L.
    Zhang, Y. S.
    MATERIALS & DESIGN, 2008, 29 (01) : 279 - 283
  • [24] Analysis of Failure Modes of Resistance Spot Welded Dissimilar Thickness DP800/AISI 1040 Steel Joints: An Effect of Welding Current
    Sabarivasan, V.
    Sivaraj, P.
    Balasubramanian, V.
    Malarvizhi, S.
    JOURNAL OF FAILURE ANALYSIS AND PREVENTION, 2025, : 402 - 412
  • [25] Tensile properties of fiber laser welded joints of high strength low alloy and dual-phase steels at warm and low temperatures
    Parkes, D.
    Westerbaan, D.
    Nayak, S. S.
    Zhou, Y.
    Goodwin, F.
    Bhole, S.
    Chen, D. L.
    MATERIALS & DESIGN, 2014, 56 : 193 - 199
  • [26] Effect of Martensite Content on Failure Behavior of Laser Welded Dual-Phase Steel Joints During Deformation
    Huan, Peng-Cheng
    Wang, Xiao-Nan
    Yang, Lei
    Zheng, Zhi
    Hu, Zeng-Rong
    Zhang, Min
    Chen, Chang-Jun
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2019, 28 (03) : 1801 - 1809
  • [27] Effect of Martensite Content on Failure Behavior of Laser Welded Dual-Phase Steel Joints During Deformation
    Peng-Cheng Huan
    Xiao-Nan Wang
    Lei Yang
    Zhi Zheng
    Zeng-Rong Hu
    Min Zhang
    Chang-Jun Chen
    Journal of Materials Engineering and Performance, 2019, 28 : 1801 - 1809
  • [28] Failure during Sheared Edge Stretching of Dual-Phase Steels
    Levy, B. S.
    Gibbs, M.
    Van Tyne, C. J.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2013, 44A (08): : 3635 - 3648
  • [29] Failure during Sheared Edge Stretching of Dual-Phase Steels
    B. S. Levy
    M. Gibbs
    C. J. Van Tyne
    Metallurgical and Materials Transactions A, 2013, 44 : 3635 - 3648
  • [30] Resistance spot welding of coated high-strength dual-phase steels
    Tumuluru, Murali D.
    WELDING JOURNAL, 2006, 85 (08) : 31 - 37
12345