Superhydrophobic Polyester/Cotton Fabrics Modified by Barrier Discharge Plasma and Organosilanes

被引：11

作者：

Novak, Igor ^{[1
]}

Valentin, Marian ^{[1
]}

Spitalsky, Zdeno ^{[1
]}

Popelka, Anton ^{[2
]}

Sestak, Jozef ^{[3
]}

Krupa, Igor ^{[2
]}

机构：

[1] Slovak Acad Sci, Polymer Inst, Bratislava, Slovakia

[2] Qatar Univ, Ctr Adv Mat, POB 2713, Doha, Qatar

[3] VUTCH CHEMITEX, Zilina, Slovakia

来源：

POLYMER-PLASTICS TECHNOLOGY AND ENGINEERING | 2018年 / 57卷 / 05期

关键词：

Cotton; fabric; hydrophobicity; plasma treatment; polyester; silanes; sol-gel; CHEMICAL-VAPOR-DEPOSITION; SURFACE MODIFICATION; SILICA SOL; COATINGS; POLY(ETHYLENE-TEREPHTHALATE); TETRAMETHYLSILANE; TEMPERATURE; ROUGHNESS; FIBERS; FILMS;

D O I：

10.1080/03602559.2017.1289397

中图分类号：

O63 [高分子化学（高聚物）];

学科分类号：

070305 ; 080501 ; 081704 ;

摘要：

In this paper, diffuse coplanar surface barrier discharge plasma at atmospheric pressure has been used for surface modification of polyester/cotton (PESc) fabric, which was subsequently modified by sol-gel process using suitable organofunctional silanes to enhance its hydrophobicity. Modified PESc fabric surfaces were conditioned during the gelling process to obtain the permanent hydrophobicity. The contact angle of water before washing of plasma and sol-gel pretreated PESc fabric was found to be 154 degrees and 151 degrees after standardized washings. It was also demonstrated that the process is applicable at the industrial scale. [GRAPHICS] .

引用

页码：440 / 448

页数：9

共 50 条

[31] Superhydrophobic fabric mixed with polyester and cotton yarns modified by alkaline treatment and thermal aging
Kim, Hyewon
Oh, Ji-Hyun
Park, Chung Hee
TEXTILE RESEARCH JOURNAL, 2021, 91 (11-12) : 1274 - 1289
[32] DISCHARGE PRINTING OF LIGHTWEIGHT POLYESTER FABRICS
PROVOST, JR
COLOURAGE, 1987, 34 (11): : A14 - &
[33] DISCHARGE RESIST PRINTING ON POLYESTER FABRICS
BAPAT, YP
AMIN, KD
COLOURAGE, 1985, 32 (22): : 15 - 19
[34] A facile method to fabricate superhydrophobic cotton fabrics
Zhang, Ming
Wang, Shuliang
Wang, Chengyu
Li, Jian
APPLIED SURFACE SCIENCE, 2012, 261 : 561 - 566
[35] BUILD-UP OF PARTICULATE AND ORGANIC SOILS ON COTTON, POLYESTER AND POLYESTER/COTTON FABRICS
SONTAG, MS
PURCHASE, ME
SMITH, BF
AMERICAN DYESTUFF REPORTER, 1969, 58 (26): : 19 - &
[36] Multifunctional Properties of Polyester Fabrics Modified by Corona Discharge/Air RF Plasma and Colloidal TiO2 Nanoparticles
Mihailovic, D.
Saponjic, Z.
Molina, R.
Radoicic, M.
Esquena, J.
Jovancic, P.
Nedeljkovic, J.
Radetic, M.
POLYMER COMPOSITES, 2011, 32 (03) : 390 - 397
[37] EVALUATION OF ANTIMONY OXIDE ON COTTON AND COTTON/POLYESTER FABRICS.
Timpa, Judy D.
Goynes Jr., Wilton R.
Chance, Leon H.
Journal of Fire Retardant Chemistry, 1979, 6 : 55 - 65
[38] EVALUATION OF ANTIMONY OXIDE ON COTTON AND COTTON-POLYESTER FABRICS
TIMPA, JD
GOYNES, WR
CHANCE, LH
JOURNAL OF FIRE RETARDANT CHEMISTRY, 1979, 6 (01): : 55 - 65
[39] Self-cleaning properties of titanium dioxide modified polyester/cotton blend fabrics
Chen W.
Zhang H.
Chen T.
Wu H.
Zhang, Hui (hzhangw532@xpu.edu.cn), 1600, China Textile Engineering Society (41): : 122 - 128and134
[40] Fabrication of Durably Superhydrophobic Cotton Fabrics by Atmospheric Pressure Plasma Treatment with a Siloxane Precursor
Yang, Jing
Pu, Yi
Miao, Dagang
Ning, Xin
POLYMERS, 2018, 10 (04)

← 1 2 3 4 5 →