Fabrication of composite material using alumina agglomerated sludge and aluminum powder by spark plasma sintering

被引：9
|
作者：
Fukumoto, I [1 ]
Mekaru, S [1 ]
Shibata, S [1 ]
Nakayama, K [1 ]
机构：
[1] Univ Ryukyus, Dept Mech Syst Engn, Nishihara, Okinawa 9012215, Japan
来源：
JSME INTERNATIONAL JOURNAL SERIES A-SOLID MECHANICS AND MATERIAL ENGINEERING | 2006年 / 49卷 / 01期
关键词：
powder; aluminum; alumina; spark plasma; sintering; composite; sludge;
D O I：
10.1299/jsmea.49.91
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The composite material was fabricated using alumina sludge, industry waste, and aluminum powder by spark plasma sintering (SPS). Sludge of industry waste was treated to change the a alumina crystal structure at temperature 1573 K for 2 hours. The bending strength of the composite materials was investigated by changing the volume fraction of sludge 0-6% and forming conditions. As a result, it was found that the sludge content mainly affected on the bending strength. The bending strength showed the highest value at 2% sludge content. From the observation of crack propagation using optical microscope, it became clear that the sludge existed as agglomerated powder in the composite material, and this sludge prevented the crack to propagate.
引用
收藏
页码：91 / 94
页数：4
相关论文
共 50 条
  • [21] Spark Plasma Sintering of Nanostructured Aluminum: Influence of Tooling Material on Microstructure
    Liu, Dongming
    Xiong, Yuhong
    Li, Ying
    Topping, Troy D.
    Zhou, Yizhang
    Haines, Chris
    Paras, Joseph
    Martin, Darold
    Kapoor, Deepak
    Schoenung, Julie M.
    Lavernia, Enrique J.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2013, 44A (04): : 1908 - 1916
  • [22] Spark plasma sintering of silicon nitride/barium aluminum silicate composite
    Bahrami, S.
    Zakeri, M.
    Faeghinia, A.
    Rahimipour, M. R.
    CERAMICS INTERNATIONAL, 2017, 43 (12) : 9153 - 9157
  • [23] Spark plasma sintering of iron powder
    Sueyoshi, Hidekazu
    Maruno, Tomobito
    Maeda, Yasushi
    Onomoto, Tatsuro
    Transactions of the Materials Research Society of Japan, Vol 31, No 4, 2006, 31 (04): : 859 - 864
  • [24] Fabrication of Carbon Nanotube Reinforced Aluminum Matrix Composite by Spark Plasma Sintering and Hot Extrusion Hybrid Process
    Kurita, Hiroki
    Kwon, Hansang
    Kawasaki, Akira
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2011, 75 (04) : 259 - 264
  • [25] Effect of Current Pathways During Spark Plasma Sintering of an Aluminum Alloy Powder
    Frank Kellogg
    Brandon McWilliams
    Kyu Cho
    Metallurgical and Materials Transactions A, 2016, 47 : 6353 - 6367
  • [26] Effect of Aluminum Oxide Powder Particle Size on Spark Plasma Sintering Results
    Rubinkovskii, N. A.
    Shornikov, D. P.
    Tenishev, A., V
    Zaluzhnyi, A. G.
    Zholnin, A. G.
    GLASS AND CERAMICS, 2019, 76 (3-4) : 94 - 98
  • [27] Effect of Aluminum Oxide Powder Particle Size on Spark Plasma Sintering Results
    N. A. Rubinkovskii
    D. P. Shornikov
    A. V. Tenishev
    A. G. Zaluzhnyi
    A. G. Zholnin
    Glass and Ceramics, 2019, 76 : 94 - 98
  • [28] Fabrication of powder components with internal channels by spark plasma sintering and additive manufacturing
    Torresani, Elisa
    Carrillo, Maricruz
    Haines, Chris
    Martin, Darold
    Olevsky, Eugene
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2023, 43 (03) : 1117 - 1126
  • [29] Effect of Current Pathways During Spark Plasma Sintering of an Aluminum Alloy Powder
    Kellogg, Frank
    McWilliams, Brandon
    Cho, Kyu
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2016, 47A (12): : 6353 - 6367
  • [30] Spark plasma sintering using calcareous waste concrete powder
    Kanda, Yasuyuki
    CONSTRUCTION AND BUILDING MATERIALS, 2022, 349
12345