Corrosion behavior and mechanism of 3Cr steel in CO2 environment with various Ca2+ concentration

被引：25
|
作者：
Wang, Bei [1 ]
Xu, Lining [1 ]
Liu, Guozhang [1 ]
Lu, Minxu [1 ]
机构：
[1] Univ Sci & Technol Beijing, Inst Adv Mat & Technol, Corros & Protect Ctr, Key Lab Environm Fracture MOE, Beijing 100083, Peoples R China
来源：
CORROSION SCIENCE | 2018年 / 136卷
关键词：
Low alloy steel; Weight loss; Polarization; Acid corrosion; Passivity; IRON-CHROMIUM-ALLOYS; ELECTRODE IMPEDANCES; INTERNAL CORROSION; ANODIC-DISSOLUTION; PIPELINE STEEL; GAS-PIPELINES; CALCIUM-IONS; CARBON-STEEL; PRESSURE; TEMPERATURE;
D O I：
10.1016/j.corsci.2018.03.013
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effect of Ca2+ on the corrosion behavior of 3Cr steel was investigated using immersion tests and electrochemical measurements. The results demonstrated that with an increase in Ca2+ concentration in the solution, the corrosion rate of 3Cr steel decreased and the Ca2+ content in the corrosion scale increased. Ca is involved in the formation of both the inner and outer corrosion scales of 3Cr steel. Polarization curves revealed that Ca2+ could enhance the pseudopassivation of 3Cr steel. EIS results demonstrated that Ca2+ can decrease the porosity of corrosion films. Additionally, Ca2+ could accelerate the precipitation of FeCO3 (CaxFe1-xCO3) by reducing its solubility and saturation degree.
引用
收藏
页码：210 / 220
页数：11
相关论文
共 50 条
  • [41] Effect of Ca2+ on CO2 corrosion properties of X65 pipeline steel
    Chen Ding1)
    InternationalJournalofMineralsMetallurgyandMaterials, 2009, 16 (06) : 661 - 666
  • [42] Alloy design employing Ni and Mo low alloying for 3Cr steel with enhanced corrosion resistance in CO2 environments
    Zhang, Shaohua
    Bian, Tiantian
    Mou, Liming
    Yan, Xiaoyan
    Zhang, Jinling
    Zhang, Yuezhong
    Liu, Baosheng
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2023, 24 : 1304 - 1321
  • [43] Characterization of corrosion scale formed on 3Cr steel in CO2-saturated formation water
    Guo, Shaoqiang
    Xu, Lining
    Zhang, Lei
    Chang, Wei
    Lu, Minxu
    CORROSION SCIENCE, 2016, 110 : 123 - 133
  • [44] INFLUENCE OF CR CONTENT IN STEEL ON CO2 CORROSION
    UEDA, M
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1984, 70 (13): : 1357 - 1357
  • [45] Effect of typical ions on the corrosion behavior of carbon steel in CO2 environment
    Gu T.
    Tang D.
    Wang Z.
    Chen H.
    Xie H.
    Natural Gas Industry, 2019, 39 (07) : 106 - 112
  • [46] Observation and analysis of pseudopassive film on 6.5%Cr steel in CO2 corrosion environment
    Wang, Bei
    Xu, Lining
    Zhu, Jinyang
    Xiao, Hui
    Lu, Minxu
    CORROSION SCIENCE, 2016, 111 : 711 - 719
  • [47] Corrosion Inhibition Mechanism of Carbon Steel in O2/CO2 Coexisting Environment
    Wang B.
    Xu L.-N.
    Li D.-Y.
    Lu M.-X.
    Cailiao Gongcheng/Journal of Materials Engineering, 2017, 45 (05): : 38 - 45
  • [48] Corrosion behavior of a 3 % Cr tubing steel in a CO2 saturated high-salinity brine
    Luo, Zhihua
    Yan, Wei
    Zhu, Peike
    Guan, Lei
    Wang, Kongyang
    Ye, Sutao
    Xu, Xuerui
    MATERIALS TESTING, 2018, 60 (03) : 245 - 250
  • [49] Effect of Cr content on the corrosion performance of low-Cr alloy steel in a CO2 environment
    Xu, Lining
    Wang, Bei
    Zhu, Jinyang
    Li, Wei
    Zheng, Ziyi
    APPLIED SURFACE SCIENCE, 2016, 379 : 39 - 46
  • [50] A flow loop study on the effect of Ca2+ ions on the CO2 corrosion of 1Cr carbon steel in a CaCO3-saturated solution
    Rizzo, Riccardo
    Palencsar, Attila
    Ambat, Rajan
    CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2021, 56 (08) : 787 - 795
12345