Corrosion behavior and mechanism of 3Cr steel in CO2 environment with various Ca2+ concentration

被引：25
|
作者：
Wang, Bei [1 ]
Xu, Lining [1 ]
Liu, Guozhang [1 ]
Lu, Minxu [1 ]
机构：
[1] Univ Sci & Technol Beijing, Inst Adv Mat & Technol, Corros & Protect Ctr, Key Lab Environm Fracture MOE, Beijing 100083, Peoples R China
来源：
CORROSION SCIENCE | 2018年 / 136卷
关键词：
Low alloy steel; Weight loss; Polarization; Acid corrosion; Passivity; IRON-CHROMIUM-ALLOYS; ELECTRODE IMPEDANCES; INTERNAL CORROSION; ANODIC-DISSOLUTION; PIPELINE STEEL; GAS-PIPELINES; CALCIUM-IONS; CARBON-STEEL; PRESSURE; TEMPERATURE;
D O I：
10.1016/j.corsci.2018.03.013
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effect of Ca2+ on the corrosion behavior of 3Cr steel was investigated using immersion tests and electrochemical measurements. The results demonstrated that with an increase in Ca2+ concentration in the solution, the corrosion rate of 3Cr steel decreased and the Ca2+ content in the corrosion scale increased. Ca is involved in the formation of both the inner and outer corrosion scales of 3Cr steel. Polarization curves revealed that Ca2+ could enhance the pseudopassivation of 3Cr steel. EIS results demonstrated that Ca2+ can decrease the porosity of corrosion films. Additionally, Ca2+ could accelerate the precipitation of FeCO3 (CaxFe1-xCO3) by reducing its solubility and saturation degree.
引用
收藏
页码：210 / 220
页数：11
相关论文
共 50 条
  • [1] Corrosion of 3Cr Steel in Supercritical CO2 Systems
    Zhang, Yucheng
    Meng, Yang
    Ju, Xinhua
    Jiang, Zhonghang
    Ma, Zejun
    Wei, Liang
    Gao, Kewei
    MATERIALS PERFORMANCE, 2019, 58 (04) : 50 - 53
  • [2] Effect of free Cr content on corrosion behavior of 3Cr steels in a CO2 environment
    Li, Wei
    Xu, Lining
    Qiao, Lijie
    Li, Jinxu
    APPLIED SURFACE SCIENCE, 2017, 425 : 32 - 45
  • [3] Effect of silty sand with different sizes on corrosion behavior of 3Cr steel in CO2 aqueous environment
    Liu, Wei
    Lu, Songle
    Zhang, Peng
    Dou, Juanjuan
    Zhao, Qinghe
    APPLIED SURFACE SCIENCE, 2016, 379 : 163 - 170
  • [4] Study on Corrosion Behavior of 3Cr Steel in an O2-containing CO2Environment
    Wang, Fan
    Zhao, Guoxian
    Fang, Kun
    Pei, Wenxia
    Ding, Langyong
    Liu, Ranran
    Cailiao Daobao/Materials Reports, 2024, 38 (23):
  • [5] EXPERIMENTAL STUDY OF CO2 CORROSION OF 3Cr PIPE LINE STEEL
    Guo Shaoqiang
    Xu Lining
    Chang Wei
    Mi Yarong
    Lu Minxu
    ACTA METALLURGICA SINICA, 2011, 47 (08) : 1067 - 1074
  • [6] Characteristics of Corrosion Scale of 3Cr Steel at High Temperature and Pressure in an O2 and CO2 Environment
    Lin Xue-Qiang
    Liu Wei
    Zhang Jing
    Dong Shuai
    Zhang Hai-Long
    Li Xiao-Bo
    Xu Chuan-Chuan
    Lu Min-Xu
    ACTA PHYSICO-CHIMICA SINICA, 2013, 29 (11) : 2405 - 2414
  • [7] Effect of pH on the corrosion and electrochemical behavior of 3Cr steel in CO2 saturated NaCl solution
    Jia, Zhijun
    Du, Cuiwei
    Liu, Zhiyong
    Gao, Jin
    Li, Xiaogang
    Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research, 2011, 25 (01): : 39 - 44
  • [8] Role of Trace Dissolved Oxygen Content in Corrosion Scale of 3Cr Steel in CO2 Aqueous Environment
    Longjun Chen
    Wei Liu
    Baojun Dong
    Peng Zhang
    Qinghe Zhao
    Tianyi Zhang
    Pengcheng Fan
    Hai Li
    Journal of Materials Engineering and Performance, 2022, 31 : 4864 - 4876
  • [9] Damage analysis of rotation speed on corrosion film of 3Cr steel in the CO2 environment with silty sand
    Zhao, Yonggang
    Liu, Wei
    Dong, Baojun
    Chen, Longjun
    Fan, Yueming
    Zhang, Tianyi
    Yang, Weijian
    ENGINEERING FAILURE ANALYSIS, 2022, 133
  • [10] Role of Trace Dissolved Oxygen Content in Corrosion Scale of 3Cr Steel in CO2 Aqueous Environment
    Chen, Longjun
    Liu, Wei
    Dong, Baojun
    Zhang, Peng
    Zhao, Qinghe
    Zhang, Tianyi
    Fan, Pengcheng
    Li, Hai
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2022, 31 (06) : 4864 - 4876
12345