Evaluation of epoxy-based coating degradation under thermal insulation at elevated temperatures on different steel substrates

被引:9
|
作者
Cao, Qing [1 ]
Oluwoye, Ibukun [1 ]
Pojtanabuntoeng, Thunyaluk [1 ]
Farhat, Hanan [2 ]
Iannuzzi, Mariano [1 ]
机构
[1] Curtin Univ, Curtin Corros Ctr, Curtin Univ, WA 6102, Australia
[2] Hamad Bin Khalifa Univ, Qatar Environm & Energy Res Inst, Corros Ctr, Ar Rayyan, Qatar
关键词
Corrosion under insulation; Coating; Coating degradation;
D O I
10.1016/j.porgcoat.2023.107544
中图分类号
O69 [应用化学];
学科分类号
081704 ;
摘要
Corrosion under insulation (CUI) remains one of the most critical issues in the petrochemical industry. In a typical CUI system, protective coatings (organic or metallic) are used primarily as the last barrier to prevent the rapid corrosion of the metallic substrate. However, organic coatings exposed to high operating temperatures and thermal cycling conditions are susceptible to failure and thus require coating performance evaluations under representative thermal insulation conditions. This study presents experimental designs to investigate the degradation of an organic polyamine-cured epoxy coating under accelerated laboratory test conditions. Additionally, a systematic CUI evaluation protocol for high-temperature organic coating performance is presented. The method involved specially designed apparatus to simulate CUI systems and characterisation techniques, such as visual inspection, adhesion test, peel-off test, scanning electron microscopy, electrochemical impedance spectroscopy, and chemical analysis using Fourier-transform infrared spectroscopy, and differential scanning calorimetry. The results showed that polyamine-based epoxy coating experienced thermal degradation starting at temperatures above 130 degrees C under mineral wool insulation in accelerated and cyclic CUI tests. Chemical degradation was the primary mode of degradation, with the formation of carbonyl functional groups and increased glass transition temperature observed at higher exposure temperatures. The proposed combination of electrochemical, spectroscopic, mechanical, and microscopy techniques allows quantifying coating performance under insulation and subsequently provides insights into predicting coatings' service lifetime.
引用
收藏
页数:13
相关论文
共 50 条
  • [31] Assessment of unexplored isoconversional methods to predict epoxy-based composite curing under arbitrary thermal histories
    Ruiz, Jose Antonio Gonzalez
    Farjas, Jordi
    Blanco, Norbert
    Costa, Josep
    Gascons, Marc
    JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 2023, 42 (19-20) : 1067 - 1074
  • [32] Epoxy-Based nanocomposite coating reinforced by a zeolite complex: Its anticorrosion properties on mild steel in 3.5 wt% NaCl media
    Khodaei, Parisa
    Shabani-Nooshabadi, Mehdi
    Behpour, Mohsen
    PROGRESS IN ORGANIC COATINGS, 2019, 136
  • [33] Evaluation of a sulfursilane anticorrosive pretreatment on galvannealed steel compared to phosphate under a waterborne epoxy coating
    Francisco, J. S.
    Capelossi, V. R.
    Aoki, I. V.
    ELECTROCHIMICA ACTA, 2014, 124 : 128 - 136
  • [34] Thermo-mechanical performance of wolframite mineral reinforced siloxane-modified epoxy-based intumescent coating for structural steel
    Lee, Yuan Xien
    Ahmad, Faiz
    Karuppanan, Saravanan
    Sumby, Christopher
    Shahed, Chowdhury Ahmed
    Ramli, Siti Haslina
    POLYMERS FOR ADVANCED TECHNOLOGIES, 2024, 35 (01)
  • [35] A comparative study of corrosion resistance of epoxy-based coating incorporated chitosan, silica and hybrid compound of chitosan/silica on mild steel
    Ma, Iling Aema Wonnie
    Kumar, Sachin Sharma Ashok
    Kasi, Ramesh
    Shafaamri, Ammar
    Subramaniam, Ramesh
    PIGMENT & RESIN TECHNOLOGY, 2022,
  • [36] EVALUATION OF DEGRADATION AT ELEVATED-TEMPERATURES OF CR-MO-V STEEL BY LOCAL RECOVERY PHENOMENA
    KIMURA, K
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 71 : 1339 - 1339
  • [37] Insulation Characteristics and Failure Mechanism of High-Voltage Cables under Different Thermal Aging Temperatures
    Duan Y.
    Han M.
    Wang Z.
    Lan R.
    Li G.
    Diangong Jishu Xuebao/Transactions of China Electrotechnical Society, 2024, 39 (01): : 45 - 54
  • [38] COLLAPSE BEHAVIOR EVALUATION OF STEEL FLOOR STRUCTURES WITH UNINSULATED SECONDARY BEAMS UNDER ELEVATED TEMPERATURES IN FIRES
    Takagi J.
    Wang S.
    Kurihara J.
    Kohno M.
    Matsuyama K.
    Journal of Structural and Construction Engineering, 2022, 87 (799): : 944 - 953
  • [39] Experimental evaluation of the thermal degradation of solar salt under different gas covers
    Prieto, Cristina
    Lopez-Roman, Anton
    Cabeza, Luisa F.
    JOURNAL OF ENERGY STORAGE, 2023, 72
  • [40] Thermal performance of hybrid fibers reinforced epoxy based intumescent coating for fire resistance of steel structures
    Yasir M.
    Ahmad F.
    Materials Research Innovations, 2023, 27 (05) : 330 - 341