Influence of Ni content on the oxidation behavior of alumina-forming Co-based oxide dispersion strengthened superalloys at 900 °C

被引：7
|
作者：
Yu, Hao [1 ]
Kondo, Sosuke [1 ]
Kasada, Ryuta [1 ]
Ukai, Shigeharu [2 ]
机构：
[1] Tohoku Univ, Inst Mat Res, Sendai 9808577, Japan
[2] Hokkaido Univ, Grad Sch Engn, Sapporo 0608628, Japan
来源：
CORROSION SCIENCE | 2023年 / 212卷
关键词：
Co-based superalloys; ODS; Alumina; TEM; HIGH-TEMPERATURE OXIDATION; DIFFUSION; NICKEL; SCALES; MICROSTRUCTURE; TRANSIENT; MECHANISM;
D O I：
10.1016/j.corsci.2022.110933
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
This work systematically investigated the effect of Ni additions of 10, 20 and 30 at% on the oxidation behavior of oxide dispersion-strengthened (ODS) Co-20Cr-15Al (at%) superalloys at 900 degrees C in air. Alumina scale with a duplex structure consisting of outer 8-alumina and inner alpha-alumina was formed on all tested Co-based ODS superalloys. Ni addition reduced the oxidation rate by inhibiting the growth of the outer 8-alumina during initial oxidation and the inner alpha-alumina during prolonged exposure. Cr2O3 formation between the interface of the 8 -and alpha-alumina layers was confirmed with the increase of Ni content.
引用
收藏
页数：14
相关论文
共 50 条
  • [21] Effects of trace elements Hf and Si on oxidation behavior of Co-Ni-Al-W-based superalloys at 900°C
    Zhou, Fanjie
    Ma, Chunmei
    Zhang, Yuheng
    Wang, Jialu
    Fu, Huadong
    ANTI-CORROSION METHODS AND MATERIALS, 2022, 69 (05) : 532 - 539
  • [22] Effects of Cr and Si addition on the high-temperature oxidation resistance in high-Mn alumina-forming oxide dispersion strengthened austenitic steels
    Geng, Diancheng
    Yu, Hao
    Yuan, Xinwei
    Kondo, Sosuke
    Miyazawa, Junichi
    Kasada, Ryuta
    NUCLEAR MATERIALS AND ENERGY, 2024, 38
  • [23] Effect of Ta on selective oxidation behavior and oxide film adhesion of alumina-forming austenitic alloys
    Chen, Lang
    Xiao, Yuanbin
    Liu, Ya
    Wu, Changjun
    Su, Xuping
    JOURNAL OF ALLOYS AND COMPOUNDS, 2024, 1008
  • [24] Low cycle fatigue of a γ'-strengthened Co-based single crystal superalloy at 900 °C
    He, Jinshan
    Wang, Xuanlei
    Zhou, Haijing
    Wang, Xitao
    MATERIALS CHARACTERIZATION, 2022, 185
  • [25] Oxidation Behavior of Fe-Ni-Co Based Superalloys and Influence of Yttrium Addition
    Jiansheng WU+
    JournalofMaterialsScience&Technology, 2000, (05) : 509 - 513
  • [26] Oxidation behavior of Fe-Ni-Co based superalloys and influence of yttrium addition
    Wu, JS
    Zhang, LT
    Zhou, JB
    Xu, Y
    Zhang, SW
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2000, 16 (05) : 509 - 513
  • [27] Corrosion behavior of new type Co-based superalloys with different Ni contents
    Gao, Bo
    Wang, Lei
    Liu, Yang
    Song, Xiu
    Yang, Shu-Yu
    Yao, Zhi-Yuan
    CORROSION REVIEWS, 2017, 35 (06) : 455 - 462
  • [28] Oxidation Behavior of Oxide Dispersion-Strengthened W-Ni Alloys
    Talekar, V. R.
    Patra, A.
    Sahoo, S. K.
    OXIDATION OF METALS, 2020, 93 (1-2): : 17 - 28
  • [29] Influence of Co to Ni ratio in γ′-strengthened model alloys on oxidation resistance and the efficacy of the halogen effect at 900 °C
    Weiser, Martin
    Galetz, Mathias C.
    Zschau, Hans-Eberhard
    Zenk, Christopher H.
    Neumeier, Steffen
    Goken, Mathias
    Virtanen, Sannakaisa
    CORROSION SCIENCE, 2019, 156 : 84 - 95
  • [30] Oxide Dispersion Strengthened Bond Coats with Higher Alumina Content: Oxidation Resistance and Influence on Thermal Barrier Coating Lifetime
    Vorkoetter, C.
    Hagen, S. P.
    Pintsuk, G.
    Mack, D. E.
    Virtanen, S.
    Guillon, O.
    Vassen, R.
    OXIDATION OF METALS, 2019, 92 (3-4): : 167 - 194
12345