High temperature oxidation behavior of TiAl alloy with electrodeposited SiOC coating

被引：8
|
作者：
Yan, Hao-Jie [1 ]
Li, Yun-Yang [1 ]
Yin, Ruo-Zhan [1 ]
Sun, Qing-Qing [1 ]
Liu, Hui-Jun [2 ]
Zeng, Chao-Liu [2 ]
Wu, Lian-Kui [1 ]
Cao, Fa-He [1 ]
机构：
[1] Sun Yat Sen Univ, Sch Mat, Shenzhen 518107, Peoples R China
[2] Songshan Lake Mat Lab, Dongguan 523808, Peoples R China
来源：
CORROSION SCIENCE | 2023年 / 224卷
基金：
中国国家自然科学基金;
关键词：
TiAl; SiOC coating; High temperature oxidation; Free carbon; Selective oxidation; SILICON OXYCARBIDE GLASSES; CERAMIC COATINGS; SIALOC GLASSES; RESISTANCE; SILANE; IMPROVEMENT; PRECURSOR; MICROSTRUCTURE; BARRIER;
D O I：
10.1016/j.corsci.2023.111491
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
SiOC coating was electrodeposited on TiAl alloy to improve the high temperature oxidation resistance. The mass gain of the compact SiOC coating is 0.06 +/- 0.026 mg cm-2, which is one order of magnitude lower than that of TiAl alloy. The SiOC coating exhibits good thermal stability and partial amorphous SiOC transforms into crystal SiO2 or SiC. After oxidation, no obvious pore can be found in the coating. Moreover, an Al2O3 layer is generated due to the enrichment of Al and the low oxygen partial pressure at the coating/substrate interface, therefore improving the barrier property of the oxide scale.
引用
收藏
页数：12
相关论文
共 50 条
  • [21] An Al+Y Coating Process for Improvement of the High-Temperature Oxidation Resistance of a TiAl Alloy
    H. G. Jung
    D. M. Wee
    M. H. Oh
    K. Y. Kim
    Oxidation of Metals, 2001, 55 : 189 - 208
  • [22] An Al plus Y coating process for improvement of the high-temperature oxidation resistance of a TiAl alloy
    Jung, HG
    Wee, DM
    Oh, MH
    Kim, KY
    OXIDATION OF METALS, 2001, 55 (3-4): : 189 - 208
  • [23] Effect of rhenium on corrosion behavior of electrodeposited Co-Cu alloy coating at room temperature and high temperature
    Lin, Yixuan
    Chen, Yiheng
    Tong, Zhangzhang
    Hu, Zhibiao
    Gao, Zhiming
    MATERIALS TODAY COMMUNICATIONS, 2023, 35
  • [24] Oxidation Behavior of Silicon-Aluminizing Coating on ?-TiAl Alloy at Different Temperatures
    Zhao, Feng
    Huang, Jiang
    Cui, Xinyu
    Wang, Jiqiang
    Xiong, Tianying
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2024, 33 (09) : 4447 - 4460
  • [25] Oxidation Behavior of γ-TiAl Alloy with NiCrAlY/Al Duplex Coating at 950 °C
    Xu Yi
    Miao Qiang
    Liang Wenping
    Wang Ling
    Yu Xiushui
    Jiang Qiong
    Ren Beilei
    RARE METAL MATERIALS AND ENGINEERING, 2014, 43 (06) : 1407 - 1411
  • [26] Structure and oxidation behavior of γ-TiAl coating produced by laser cladding on titanium alloy
    Maliutina, Iu. N.
    Si-Mohand, H.
    Sijobert, J.
    Bertrand, Ph.
    Lazurenko, D. V.
    Bataev, I. A.
    SURFACE & COATINGS TECHNOLOGY, 2017, 319 : 136 - 144
  • [27] High temperature oxidation behavior of tial coated by Al-Cr alloy in molten salt
    Ueda, M
    Susukida, D
    Konda, S
    Ohtsuka, T
    MOLTEN SALTS XIII, 2002, 2002 (19): : 724 - 733
  • [28] Initial oxidation behavior of TiAl alloy
    Xi, Yanjun
    Liu, Yongjun
    Lu, Jinbin
    Wang, Zhixin
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2008, 37 (12): : 2165 - 2168
  • [29] Initial Oxidation Behavior of TiAl Alloy
    Xi Yanjun
    Liu Yongjun
    Lu Jinbin
    Wang Zhixin
    RARE METAL MATERIALS AND ENGINEERING, 2008, 37 (12) : 2165 - 2168
  • [30] High-temperature tribological behavior of a NiCoCrAlY/ZrO2 duplex coating on γ-TiAl alloy
    Ding, Zheng
    Miao, Qiang
    Liang, Wenping
    Yang, Zhengang
    An, Hao
    Yi, Jinwei
    Lin, Hao
    MATERIALS RESEARCH EXPRESS, 2019, 6 (08):
12345